  • Material properties of the Pt electrode deposited on nafion membrane by the impregnation-reduction method.

Material properties of the Pt electrode deposited on nafion membrane by the impregnation-reduction method.

Journal of nanoscience and nanotechnology (2013-07-19)
Muhammad Rashid, Tae-Sun Jun, Yong Shin Kim
RESUMO

Platinum nanoparticles (Pt NPs) were chemically deposited on a Nafion polymer electrolyte membrane by the impregnation-reduction (I-R) procedure to prepare an active electrode for solid electrochemical sensors. Various analysis methods such as SEM, EDX, XRD and cyclic voltammogram (CV) measurements were employed in order to characterize microstructures and electrochemical properties of the Pt layer. At the conditions ([Pt(NH3)4Cl2] = 10 mM, [NaBH4] = 60 mM, 50 degrees C), the porous Pt thin-film, consisting of sphere-like particles formed by the agglomeration of primary polycrystalline Pt NPs with an average crystal size of 13-18 nm, was obtained and confirmed to have a large surface area (roughness factor = 267) and strong adhesion due to the formation of interfacial Pt-Nafion composites. The secondary globular particles were found to have an average diameter of 215 nm and irregular protuberances on the surface. Furthermore, this electrode exhibited well-resolved CV peaks for the hydrogen redox reactions in an acid solution, suggesting the existence of different adsorption sites and good electrochemical behaviors. Pt/Nafion electrodes were prepared under different conditions in [Pt(NH3)4Cl2], [NaBH4] and reaction temperature, and their material properties were discussed from the viewpoint of a Pt growth mechanism.

MATERIAIS
Número do produto
Marca
Descrição do produto

Sigma-Aldrich
Platinum, wire, diam. 0.5 mm, 99.99% trace metals basis
Sigma-Aldrich
Platinum, wire, diam. 0.25 mm, 99.9% trace metals basis
Sigma-Aldrich
Platinum, wire, diam. 0.5 mm, 99.9% trace metals basis
Sigma-Aldrich
Platinum, foil, thickness 0.025 mm, 99.9% trace metals basis
Sigma-Aldrich
Platinum, gauze, 100 mesh, 99.9% trace metals basis
Sigma-Aldrich
Platinum, wire, diam. 1.0 mm, 99.9% trace metals basis
Sigma-Aldrich
Platinum black, black, powder, ≤20 μm, ≥99.95% trace metals basis
Sigma-Aldrich
Platinum, gauze, 52 mesh, 99.9% trace metals basis
Sigma-Aldrich
Platinum, powder, 99.995% trace metals basis
Sigma-Aldrich
Platinum, nanopowder, <50 nm particle size (TEM)
Sigma-Aldrich
Platinum, foil, thickness 0.05 mm, 99.99% trace metals basis
Sigma-Aldrich
Platinum, wire, diam. 2.0 mm, 99.9% trace metals basis
Sigma-Aldrich
Platinum, wire, diam. 0.25 mm, 99.99% trace metals basis
Sigma-Aldrich
Platinum, wire, diam. 0.076 mm, ≥99.99% trace metals basis
Sigma-Aldrich
Platinum, foil, thickness 0.5 mm, 99.99% trace metals basis
Sigma-Aldrich
Platinum black, fuel cell grade, ≥99.9% trace metals basis
Sigma-Aldrich
Platinum, powder, ≤10 μm, 99.9% trace metals basis
Sigma-Aldrich
Platinum, foil, thickness 0.1 mm, 99.9% trace metals basis
Sigma-Aldrich
Platinum, wire, diam. 0.25 mm, thermocouple grade
Sigma-Aldrich
Platinum, foil, thickness 0.125-0.135 mm, 99.9% trace metals basis
Sigma-Aldrich
Platinum, wire, diam. 0.10 mm, 99.99% trace metals basis
Sigma-Aldrich
Platinum, wire, diam. 1.0 mm, 99.99% trace metals basis
Sigma-Aldrich
Platinum, foil, thickness 1.0 mm, 99.99% trace metals basis
Sigma-Aldrich
Platinum, evaporation slug, diam. × L 0.6 cm × 1.2 cm, 99.99% trace metals basis
Sigma-Aldrich
Platinum black, low bulk density, ≥99.9% trace metals basis
Sigma-Aldrich
Platinum, wire, diam. 0.127 mm, 99.9% trace metals basis
Sigma-Aldrich
Platinum, foil, thickness 0.05 mm, ≥99.9% trace metals basis
Sigma-Aldrich
Platinum, foil, thickness 0.127 mm, 99.99% trace metals basis
Sigma-Aldrich
Platinum, wire, diam. 0.127 mm, 99.99% trace metals basis
Sigma-Aldrich
Platinum, powder (coarse), 99.99% trace metals basis