  • Functionalized bio-artifact fabricated via selective slurry extrusion. Part 2: Fabrication of ceramic dental crown.

Functionalized bio-artifact fabricated via selective slurry extrusion. Part 2: Fabrication of ceramic dental crown.

Journal of nanoscience and nanotechnology (2014-04-17)
D B Zhu, J P Liang, Y X Qu, G L Duan
RESUMO

Functionalized ceramic dental crown was successfully fabricated through selective slurry extrusion (SSE) based technique of solid freeform fabrication (also known as rapid prototyping). After sintering, the decomposed tourmaline powders were embedded in ZrO2 matrix. The far infrared emission properties of the ceramic dental crown were improved due to the increase of the numbers of infrared active bonds from tourmaline. This new dental restoration process presents potential to provide dental patients with functionalized artificial teeth, which benefits the body health by the way of emitting far infrared rays in ambient temperatures.

MATERIAIS
Número do produto
Marca
Descrição do produto

Sigma-Aldrich
Zirconium(IV) oxide, powder, 5 μm, 99% trace metals basis
Sigma-Aldrich
Zirconium(IV) oxide, nanopowder, <100 nm particle size (TEM)
Sigma-Aldrich
Zirconium, powder, −100 mesh
Sigma-Aldrich
Zirconium, foil, thickness 0.1 mm, 99.98% trace metals basis
Sigma-Aldrich
Zirconium(IV) oxide, 99.99% trace metals basis (purity excludes ~2% HfO2)
Sigma-Aldrich
Zirconium(IV) oxide, nanoparticles, dispersion, <100 nm particle size (BET), 5 wt. % in H2O
Sigma-Aldrich
Zirconium, sponge, ≥99% trace metals basis
Sigma-Aldrich
Zirconium, rod, diam. 6.35 mm, ≥99% trace metals basis
Sigma-Aldrich
Zirconium(IV) oxide, nanoparticles, dispersion, <100 nm particle size (BET), 10 wt. % in H2O
Zirconium, rod, 100mm, diameter 50mm, centerless ground, 99.2%
Zirconium, foil, not light tested, 50x50mm, thickness 0.006mm, 99.2%
Zirconium, rod, 1000mm, diameter 1.5mm, 99.2%
Zirconium, rod, 1000mm, diameter 12.7mm, centerless ground, 99.2%
Zirconium, rod, 1000mm, diameter 2.0mm, centerless ground, 99.2%
Zirconium, rod, 1000mm, diameter 3.0mm, centerless ground, 99.2%
Zirconium, rod, 1000mm, diameter 5.0mm, centerless ground, 99.2%
Zirconium, rod, 1000mm, diameter 6.0mm, centerless ground, 99.2%
Zirconium, rod, 1000mm, diameter 9.5mm, centerless ground, 99.2%
Zirconium, rod, 100mm, diameter 1.5mm, 99.2%
Zirconium, rod, 100mm, diameter 12.7mm, centerless ground, 99.2%
Zirconium, rod, 100mm, diameter 19.0mm, centerless ground, 99.2%
Zirconium, rod, 100mm, diameter 2.0mm, centerless ground, 99.2%
Zirconium, rod, 100mm, diameter 3.0mm, centerless ground, 99.2%
Zirconium, rod, 100mm, diameter 5.0mm, centerless ground, 99.2%
Zirconium, rod, 100mm, diameter 6.0mm, centerless ground, 99.2%
Zirconium, rod, 100mm, diameter 9.5mm, centerless ground, 99.2%
Zirconium, rod, 200mm, diameter 1.5mm, 99.2%
Zirconium, rod, 200mm, diameter 12.7mm, centerless ground, 99.2%
Zirconium, rod, 200mm, diameter 19.0mm, centerless ground, 99.2%
Zirconium, rod, 200mm, diameter 2.0mm, centerless ground, 99.2%

Redes sociais

LinkedIn icon
Twitter icon
Facebook Icon
Instagram Icon

Merck

Pesquisa. Desenvolvimento. Produção.

Somos um fornecedor global líder para o setor de ciências biológicas, com soluções e serviços para pesquisa, desenvolvimento e produção de biotecnologia, além de produção e desenvolvimento de terapias farmacológicas com medicamentos.

© 2021 Merck KGaA, Darmstadt, Alemanha e/ou suas filiais. Todos os direitos reservados.

A reprodução não autorizada de quaisquer materiais deste site é estritamente proibida.