  • Fabrication of ordered poly(methyl methacrylate) nanobowl arrays using SiO2 colloidal crystal templates.

Fabrication of ordered poly(methyl methacrylate) nanobowl arrays using SiO2 colloidal crystal templates.

Journal of nanoscience and nanotechnology (2014-04-18)
Lier Deng, Ming Fu, Yinglei Tao, Xiaoyun Guo
RESUMO

A simple approach is presented for the fabrication of poly(methyl methacrylate) (PMMA) nanobowl arrays over cm2 areas using SiO2 colloidal crystal templates. SiO2 colloidal crystal templates were prepared on a clean glass substrate by self-assembled SiO2 spheres of 410 nm in diameter. The air between the silica spheres was filled by the superfluous monomer of PMMA that can be subsequently polymerized. After infiltration, the SiO2-PMMA templates were immersed in a 3 wt% hydrofluoric acid (HF) aqueous solution. After 24 h, silica spheres were etched and a free-standing nanobowl sheet was obtained. The size of the nanobowls could be controlled by the size of the SiO2 spheres and the area of the nanobowl sheet could be altered by the size of the glass substrate.

MATERIAIS
Número do produto
Marca
Descrição do produto

Sigma-Aldrich
Poly(methyl methacrylate), average Mw ~120,000 by GPC
Sigma-Aldrich
Silicon dioxide, nanopowder, 10-20 nm particle size (BET), 99.5% trace metals basis
Sigma-Aldrich
Poly(methyl methacrylate), average Mw ~350,000 by GPC
Sigma-Aldrich
LUDOX® HS-40 colloidal silica, 40 wt. % suspension in H2O
Sigma-Aldrich
Poly(methyl methacrylate), average Mw ~15,000 by GPC, powder
Sigma-Aldrich
LUDOX® AS-40 colloidal silica, 40 wt. % suspension in H2O
Sigma-Aldrich
Poly(methyl methacrylate)
Sigma-Aldrich
Silica, nanoparticles, mesoporous, 200 nm particle size, pore size 4 nm
Sigma-Aldrich
LUDOX® TM-50 colloidal silica, 50 wt. % suspension in H2O
Sigma-Aldrich
Silicon dioxide, nanopowder (spherical, porous), 5-20 nm particle size (TEM), 99.5% trace metals basis
Sigma-Aldrich
Silica, mesostructured, MCM-41 type (hexagonal)
Sigma-Aldrich
LUDOX® AM colloidal silica, 30 wt. % suspension in H2O
Sigma-Aldrich
Silica, nanopowder, spec. surface area 175-225 m2/g (BET), 99.8% trace metals basis
Sigma-Aldrich
LUDOX® SM colloidal silica, 30 wt. % suspension in H2O
Sigma-Aldrich
LUDOX® HS-30 colloidal silica, 30 wt. % suspension in H2O
Sigma-Aldrich
LUDOX® TMA colloidal silica, 34 wt. % suspension in H2O
Sigma-Aldrich
LUDOX® TM-40 colloidal silica, 40 wt. % suspension in H2O
Sigma-Aldrich
LUDOX® AS-30 colloidal silica, 30 wt. % suspension in H2O
Sigma-Aldrich
LUDOX® CL colloidal silica, 30 wt. % suspension in H2O
Supelco
Poly(methyl methacrylate), analytical standard, for GPC, 2,000
Sigma-Aldrich
Silica
Sigma-Aldrich
LUDOX® LS colloidal silica, 30 wt. % suspension in H2O
Sigma-Aldrich
Silica, mesostructured, MSU-F (cellular foam)
Supelco
Poly(methyl methacrylate), analytical standard, for GPC, 2,480,000
Sigma-Aldrich
Poly(methyl methacrylate), isotactic, >80% isotactic
Sigma-Aldrich
LUDOX® CL-X colloidal silica, 45 wt. % suspension in H2O
Supelco
Poly(methyl methacrylate), analytical standard, for GPC, 20,000
Supelco
Poly(methyl methacrylate), analytical standard, for GPC, 50,000
Supelco
Poly(methyl methacrylate), analytical standard, for GPC, 100,000
Supelco
Poly(methyl methacrylate), analytical standard, for GPC, 10,000