Sorptive extraction using polydimethylsiloxane/metal-organic framework coated stir bars coupled with high performance liquid chromatography-fluorescence detection for the determination of polycyclic aromatic hydrocarbons in environmental water samples.

Sorptive extraction using polydimethylsiloxane/metal-organic framework coated stir bars coupled with high performance liquid chromatography-fluorescence detection for the determination of polycyclic aromatic hydrocarbons in environmental water samples.

Journal of chromatography. A (2014-07-09)

Cong Hu, Man He, Beibei Chen, Cheng Zhong, Bin Hu

ABSTRACT

In this work, metal-organic frameworks (MOFs, Al-MIL-53-NH₂) were synthesized via the hydrothermal method, and novel polydimethylsiloxane/metal-organic framework (PDMS/MOFs, PDMS/Al-MIL-53-NH₂)-coated stir bars were prepared by the sol-gel technique. The preparation reproducibility of the PDMS/MOFs-coated stir bar was good, with relative standard deviations (RSDs) ranging from 4.8% to 14.9% (n=7) within one batch and from 6.2% to 16.9% (n=6) among different batches. Based on this fact, a new method of PDMS/MOFs-coated stir bar sorptive extraction (SBSE) and ultrasonic-assisted liquid desorption (UALD) coupled with high performance liquid chromatography-fluorescence detection (HPLC-FLD) was developed for the determination of polycyclic aromatic hydrocarbons (PAHs) in environmental water samples. To obtain the best extraction performance for PAHs, several parameters affecting SBSE, such as extraction time, stirring rate, and extraction temperature, were investigated. Under optimal experimental conditions, wide linear ranges and good RSDs (n=7) were obtained. With enrichment factors (EFs) of 16.1- to 88.9-fold (theoretical EF, 142-fold), the limits of detection (LODs, S/N=3) of the developed method for the target PAHs were found to be in the range of 0.05-2.94 ng/L. The developed method was successfully applied to the analysis of PAHs in Yangtze River and East Lake water samples.

MATERIALS

Product Number

Brand

Product Description

S0600000

Silicone oil, European Pharmacopoeia (EP) Reference Standard

GF14206047

Aluminum, foam, 33x140mm, thickness 20mm, bulk density 0.2g/cm³, porosity 0.93, aluminum 6101 grade, 98.5%

GF70010222

Aluminum, honeycomb, 150x150mm, thickness 10mm, cell size 3.2mm, cell wall 0.025mm, core density 0g/cm³, phenolic adhesive (resin), 99.5%

GF07499010

Aluminum, foam, 150x150mm, thickness 10mm, bulk density 0.2g/cm³, porosity 0.93, aluminum 6101 grade, 98.5%

GF74590724

Aluminum, honeycomb, 600x600mm, thickness 26.5mm, cell size 6.3mm, cell wall 0.064mm, core density 0.083g/cm³, phenolic adhesive (resin), facing skin glass fiber 0.5mm, 99.9%

GF12106897

Aluminum, foam, 150x150mm, thickness 6.35mm, bulk density 0.2g/cm³, porosity 0.93, 4 pores/cm, aluminum 6101 grade, 98.5%

GF46654375

Aluminum, honeycomb, 600x600mm, thickness 13.9mm, cell size 6.3mm, cell wall 0.064mm, core density 0.083g/cm³, phenolic adhesive (resin), facing skin aluminum 0.55mm, 99.9%

GF51278070

Aluminum, honeycomb, 300x300mm, thickness 10mm, cell size 3.2mm, cell wall 0.025mm, core density 0g/cm³, phenolic adhesive (resin), 99.5%

GF26812043

Aluminum, foam, 150x150mm, thickness 3.2mm, bulk density 0.2g/cm³, porosity 0.93, 16 pores/cm, aluminum 6101 grade, 98.5%

GF31796725

Aluminum, honeycomb, 300x300mm, thickness 26.5mm, cell size 6.3mm, cell wall 0.064mm, core density 0.083g/cm³, phenolic adhesive (resin), facing skin glass fiber 0.5mm, 99.9%

GF33055185

Aluminum, foam, 150x150mm, thickness 6.35mm, bulk density 0.2g/cm³, porosity 0.93, 16 pores/cm, aluminum 6101 grade, 98.5%

GF99626103

Aluminum, honeycomb, 600x600mm, thickness 20mm, cell size 4.8mm, cell wall 0.038mm, core density 0.070g/cm³, phenolic adhesive (resin), 99.5%

GF11843344

Aluminum, tube, 200mm, outside diameter 0.6mm, inside diameter 0.3mm, wall thickness 0.15mm, as drawn, 99.5%

GF41758982

Aluminum, microfoil, disks, 10mm, thinness 1.0μm, specific density 269.9μg/cm², permanent mylar 3.5μm support, 99.999%

GF63629219

Aluminum, tube, 500mm, outside diameter 1.42mm, inside diameter 1.166mm, wall thickness 0.127mm, as drawn, 99.5%

GF25360354

Aluminum, rod, 50mm, diameter 30.0mm, as drawn, 99.999%

GF90679191

Aluminum, rod, 1000mm, diameter 12.0mm, as drawn, 99.999%

GF04958084

Aluminum, honeycomb, 300x300mm, thickness 5mm, cell size 3.2mm, cell wall 0.025mm, core density 0.072g/cm³, phenolic adhesive (resin), 99.5%

GF19881928

Aluminum, honeycomb, 300x300mm, thickness 20mm, cell size 3.2mm, cell wall 0.025mm, core density 0.072g/cm³, phenolic adhesive (resin), 99.5%

GF04614724

Aluminum, honeycomb, 600x600mm, thickness 10mm, cell size 3.2mm, cell wall 0.025mm, core density 0g/cm³, phenolic adhesive (resin), 99.5%

GF80027737

Aluminum, honeycomb, 600x600mm, thickness 26.5mm, cell size 6.3mm, cell wall 0.064mm, core density 0.083g/cm³, phenolic adhesive (resin), facing skin aluminum 0.55mm, 99.9%

GF10162066

Aluminum, microleaf disks, 10mm, thinness 0.15μm, specific density 41.28μg/cm², removable support, 99.999%

GF38294646

Aluminum, mesh, 300x300mm, nominal aperture 0.38mm, wire diameter 0.25mm, 40x40 wires/inch, open area 37%, plain weave mesh

GF62524076

Aluminum, tube, 500mm, outside diameter 1.96mm, inside diameter 1.4mm, wall thickness 0.28mm, as drawn, 99.5%

GF76893889

Aluminum, microfoil, disks, 25mm, thinness 0.1μm, specific density 25.6μg/cm², permanent mylar 3.5μm support, 99.999%

GF45982716

Aluminum, insulated wire, 10m, conductor diameter 0.1mm, insulation thickness 0.005mm, polyimide insulation, 99.95+%

GF28292687

Aluminum, rod, 1000mm, diameter 10.0mm, as drawn, 99.999%

GF44675781

Aluminum, rod, 1000mm, diameter 12.7mm, 99%

GF28435844

Aluminum, microleaf disks, 10mm, thinness 0.25μm, specific density 68.8μg/cm², removable support, 99.999%

GF02018236

Aluminum, rod, 50mm, diameter 20.0mm, as drawn, 99.999%