Merck

264113

Sigma-Aldrich

beads, diam. 2-5 mm, 99.999% trace metals basis

登录to View Organizational & Contract Pricing

Select a Size

别名:
Indium element
Empirical Formula (Hill Notation):
In
CAS号:
分子量:
114.82
EC 号:
MDL编号:
PubChem化学物质编号:
NACRES:
NA.23

蒸汽压

<0.01 mmHg ( 25 °C)

检测方案

99.999% trace metals basis

形式

beads

电阻率

8.37 μΩ-cm

直径

2-5 mm

mp

156.6 °C (lit.)

密度

7.3 g/mL at 25 °C (lit.)

SMILES string

[In]

InChI

1S/In

Inchi Key

APFVFJFRJDLVQX-UHFFFAOYSA-N

正在寻找类似产品? Visit 产品对比指南

比较类似商品

查看完整比较结果

显示差异

1 of 4

此商品
326607264091357278
Indium beads, diam. 2-5&#160;mm, 99.999% trace metals basis

Sigma-Aldrich

264113

Indium beads, diam. 2-5&#160;mm, &#8805;99.9% trace metals basis

Sigma-Aldrich

326607

Indium rod, diam. 6&#160;mm, &#8805;99.999% trace metals basis

Sigma-Aldrich

264091

Indium foil, thickness 1.0&#160;mm, 99.999% trace metals basis

Sigma-Aldrich

357278

form

beads

form

beads

form

rod

form

foil

resistivity

8.37 μΩ-cm

resistivity

8.37 μΩ-cm

resistivity

8.37 μΩ-cm

resistivity

8.37 μΩ-cm

mp

156.6 °C (lit.)

mp

156.6 °C (lit.)

mp

156.6 °C (lit.)

mp

156.6 °C (lit.)

density

7.3 g/mL at 25 °C (lit.)

density

7.3 g/mL at 25 °C (lit.)

density

7.3 g/mL at 25 °C (lit.)

density

7.3 g/mL at 25 °C (lit.)

vapor pressure

<0.01 mmHg ( 25 °C)

vapor pressure

<0.01 mmHg ( 25 °C)

vapor pressure

<0.01 mmHg ( 25 °C)

vapor pressure

<0.01 mmHg ( 25 °C)

象形图

Health hazard

警示用语:

Danger

危险声明

危险分类

STOT RE 1 Inhalation

靶器官

Lungs

储存分类代码

6.1C - Combustible, acute toxic Cat.3 / toxic compounds or compounds which causing chronic effects

WGK

WGK 1

闪点(°F)

Not applicable

闪点(°C)

Not applicable

个人防护装备

dust mask type N95 (US), Eyeshields, Gloves


Certificates of Analysis (COA)

Search for Certificates of Analysis (COA) by entering the products Lot/Batch Number. Lot and Batch Numbers can be found on a product’s label following the words ‘Lot’ or ‘Batch’.

Already Own This Product?

Documents related to the products that you have purchased in the past have been gathered in the Document Library for your convenience.

Visit the Document Library

Difficulty Finding Your Product Or Lot/Batch Number?

在网站页面上,产品编号会附带包装尺寸/数量一起显示(例如:T1503-25G)。请确保 在“产品编号”字段中仅输入产品编号 (示例: T1503).

示例

T1503
货号
-
25G
包装规格/数量

其它示例:

705578-5MG-PW

PL860-CGA/SHF-1EA

MMYOMAG-74K-13

1000309185

输入内容 1.000309185)

遇到问题?欢迎随时联系我们技术服务 寻求帮助

批号可以在产品标签上"批“ (Lot或Batch)字后面找到。

Aldrich 产品

  • 如果您查询到的批号为 TO09019TO 等,请输入去除前两位字母的批号:09019TO。

  • 如果您查询到的批号含有填充代码(例如05427ES-021),请输入去除填充代码-021的批号:05427ES。

  • 如果您查询到的批号含有填充代码(例如 STBB0728K9),请输入去除填充代码K9的批号:STBB0728。

未找到您寻找的产品?

部分情况下,可能未在线提供COA。如果搜索不到COA,可在线索取。

索取COA

其他客户在看

Slide 1 of 4

1 of 4

Indium powder, &#8722;100&#160;mesh, 99.99% trace metals basis

Sigma-Aldrich

264032

Indium wire, diam. 1.0&#160;mm, 99.995% trace metals basis

Sigma-Aldrich

357073

Gallium 99.9995% trace metals basis

Sigma-Aldrich

203319

vibrant-m

NIST3124A

Indium (In) standard solution

Yongseok Kwon et al.
Organic letters, 15(4), 920-923 (2013-02-05)
This paper documents the first example of In(III)-catalyzed selective 6-exo-dig hydroarylation of o-propargylbiaryls and their subsequent double-bond migration to obtain functionalized phenanthrenes. Electron-rich biaryl substrates undergo hydroarylation more effectively, and the substrates with various types of substituents on the alkyne
Juan Zhou et al.
Chemical communications (Cambridge, England), 49(22), 2237-2239 (2013-02-12)
A reduced graphene oxide (RGO)-ZnIn(2)S(4) nanosheet composite was successfully synthesized via an in situ controlled growth process. The as-obtained RGO-ZnIn(2)S(4) composite showed excellent visible light H(2) production activity in the absence of noble metal cocatalysts.
G W Shu et al.
Optics express, 21 Suppl 1, A123-A130 (2013-02-15)
Spatially-resolved electroluminescence (EL) images in the triple-junction InGaP/InGaAs/Ge solar cell have been investigated to demonstrate the subcell coupling effect. Upon irradiating the infrared light with an energy below bandgap of the active layer in the top subcell, but above that
Yuji Zhao et al.
Optics express, 21 Suppl 1, A53-A59 (2013-02-15)
Linear polarized electroluminescence was investigated for semipolar (3031) and (3031) InGaN light-emitting diodes (LEDs) with various indium compositions. A high degree of optical polarization was observed for devices on both planes, ranging from 0.37 at 438 nm to 0.79 at
Thirumaleshwara N Bhat et al.
Journal of nanoscience and nanotechnology, 13(1), 498-503 (2013-05-08)
The thermal oxidation process of the indium nitride (InN) nanorods (NRs) was studied. The SEM studies reveal that the cracked and burst mechanism for the formation of indium oxide (In2O3) nanostructures by oxidizing the InN NRs at higher temperatures. XRD

商品

Discovery and Single Crystal Growth of Lanthanide Intermetallics—Interplay of Synthesis and Physical Properties

Solid state and materials chemistry have made a tremendous impact and have experienced growth in recent years, particularly for rare earthcontaining materials.

Lanthanide Ions as Photon Managers for Solar Cells

Spectral conversion for solar cells is an emerging concept in the field of photovoltaics, and it has the potential to increase significantly the efficiency of solar cells. Lanthanide ions are ideal candidates for spectral conversion, due to their high luminescence efficiencies and rich energy level structure that allows for great flexibility in the upconversion and downconversion of photons in a wide spectral region (NIR-VIS-UV).

我们的科学家团队拥有各种研究领域经验,包括生命科学、材料科学、化学合成、色谱、分析及许多其他领域.

联系技术服务部门