  • Antibacterial performance of nanoscaled visible-light responsive platinum-containing titania photocatalyst in vitro and in vivo.

Antibacterial performance of nanoscaled visible-light responsive platinum-containing titania photocatalyst in vitro and in vivo.

Biochimica et biophysica acta (2013-04-02)
Yao-Hsuan Tseng, Der-Shan Sun, Wen-Shiang Wu, Hao Chan, Ming-Syuan Syue, Han-Chen Ho, Hsin-Hou Chang
摘要

Traditional antibacterial photocatalysts are primarily induced by ultraviolet light to elicit antibacterial reactive oxygen species. New generation visible-light responsive photocatalysts were discovered, offering greater opportunity to use photocatalysts as disinfectants in our living environment. Recently, we found that visible-light responsive platinum-containing titania (TiO2-Pt) exerted high performance antibacterial property against soil-borne pathogens even in soil highly contaminated water. However, its physical and photocatalytic properties, and the application in vivo have not been well-characterized. Transmission electron microscopy, energy dispersive spectroscopy, X-ray photoelectron spectroscopy, X-ray diffraction, ultraviolet-visible absorption spectrum and the removal rate of nitrogen oxides were therefore analyzed. The antibacterial performance under in vitro and in vivo conditions was evaluated. The apparent quantum efficiency for visible light illuminated TiO2-Pt is relatively higher than several other titania photocatalysts. The killing effect achieved approximately 2 log reductions of pathogenic bacteria in vitro. Illumination of injected TiO2-Pt successfully ameliorated the subcutaneous infection in mice. This is the first demonstration of in vivo antibacterial use of TiO2-Pt nanoparticles. When compared to nanoparticles of some other visible-light responsive photocatalysts, TiO2-Pt nanoparticles induced less adverse effects such as exacerbated platelet clearance and hepatic cytotoxicity in vivo. These findings suggest that the TiO2-Pt may have potential application on the development of an antibacterial material in both in vitro and in vivo settings.

材料
货号
品牌
产品描述

Sigma-Aldrich
铂, wire, diam. 0.5 mm, 99.99% trace metals basis
Sigma-Aldrich
铂, wire, diam. 0.25 mm, 99.9% trace metals basis
Sigma-Aldrich
铂, foil, thickness 0.025 mm, 99.9% trace metals basis
Sigma-Aldrich
铂, gauze, 100 mesh, 99.9% trace metals basis
Sigma-Aldrich
铂, wire, diam. 0.5 mm, 99.9% trace metals basis
Sigma-Aldrich
铂黑, black, powder, ≤20 μm, ≥99.95% trace metals basis
Sigma-Aldrich
铂, wire, diam. 1.0 mm, 99.9% trace metals basis
Sigma-Aldrich
铂, gauze, 52 mesh, 99.9% trace metals basis
Sigma-Aldrich
铂, powder, 99.995% trace metals basis
Sigma-Aldrich
铂, nanopowder, <50 nm particle size (TEM)
Sigma-Aldrich
铂, foil, thickness 0.05 mm, 99.99% trace metals basis
Sigma-Aldrich
铂, wire, diam. 2.0 mm, 99.9% trace metals basis
Sigma-Aldrich
铂, wire, diam. 0.076 mm, ≥99.99% trace metals basis
Sigma-Aldrich
铂, powder, ≤10 μm, 99.9% trace metals basis
Sigma-Aldrich
铂, wire, diam. 0.25 mm, 99.99% trace metals basis
Sigma-Aldrich
铂, foil, thickness 0.5 mm, 99.99% trace metals basis
Sigma-Aldrich
铂, wire, diam. 0.25 mm, thermocouple grade
Sigma-Aldrich
铂黑, fuel cell grade, ≥99.9% trace metals basis
Sigma-Aldrich
铂, foil, thickness 0.1 mm, 99.9% trace metals basis
Sigma-Aldrich
铂, wire, diam. 0.10 mm, 99.99% trace metals basis
Sigma-Aldrich
铂, wire, diam. 1.0 mm, 99.99% trace metals basis
Sigma-Aldrich
铂, foil, thickness 0.125-0.135 mm, 99.9% trace metals basis
Sigma-Aldrich
铂, foil, thickness 1.0 mm, 99.99% trace metals basis
Sigma-Aldrich
铂, evaporation slug, diam. × L 0.6 cm × 1.2 cm, 99.99% trace metals basis
Sigma-Aldrich
铂, wire, diam. 0.127 mm, 99.9% trace metals basis
Sigma-Aldrich
铂黑, low bulk density, ≥99.9% trace metals basis
Sigma-Aldrich
铂, wire, diam. 0.127 mm, 99.99% trace metals basis
Sigma-Aldrich
铂, powder (coarse), 99.99% trace metals basis
Sigma-Aldrich
铂, foil, thickness 0.05 mm, ≥99.9% trace metals basis
Sigma-Aldrich
铂, foil, thickness 0.127 mm, 99.99% trace metals basis