  • Hydroxyapatite coatings on nanotubular titanium dioxide thin films prepared by radio frequency magnetron sputtering.

Hydroxyapatite coatings on nanotubular titanium dioxide thin films prepared by radio frequency magnetron sputtering.

Journal of nanoscience and nanotechnology (2013-07-26)
Jinho Shin, Kwangmin Lee, Jeongtae Koh, Hyeju Son, Hyunseung Kim, Hyun-Pil Lim, Kwidug Yun, Gyejeong Oh, Seokwoo Lee, Heekyun Oh, Kyungku Lee, Gabwoon Hwang, Sang-Won Park
摘要

In this study, hydroxyapatite (HA) was coated on anodized titanium (Ti) surfaces through radio frequency magnetron sputtering in order to improve biological response of the titanium surface. All the samples were blasted with resorbable blasting media (RBM). RBM-blasted Ti surface, anodized Ti surface, as-sputtered HA coating on the anodized Ti surface, and heat-treated HA coating on the anodized Ti surface were prepared. The samples were characterized using scanning electron microscopy and X-ray photoemission spectroscopy, and biologic responses were evaluated. The top of the TiO2 nanotubes was not closed by HA particles when the coating time is less than 15 minutes. It was demonstrated that the heat-treated HA was well-crystallized and this enhanced the cell attachment of the anodized Ti surface.

材料
货号
品牌
产品描述

Sigma-Aldrich
钛, foil, thickness 0.127 mm, 99.7% trace metals basis
Sigma-Aldrich
钛, foil, thickness 0.25 mm, 99.7% trace metals basis
Sigma-Aldrich
钛, powder, <45 μm avg. part. size, 99.98% trace metals basis
Sigma-Aldrich
羟基磷灰石, puriss., meets analytical specification of Ph. Eur., BP, FCC, E341, ≥90% (calculated on glowed substance)
Sigma-Aldrich
羟基磷灰石, purum p.a., ≥90% (as Ca3(PO4)2, KT)
Sigma-Aldrich
钛, powder, −100 mesh, 99.7% trace metals basis
Sigma-Aldrich
钛, foil, thickness 0.025 mm, 99.98% trace metals basis
Sigma-Aldrich
钛, sponge, 3-19 mm, 99.5% trace metals basis
Sigma-Aldrich
钛, wire, diam. 0.25 mm, 99.7% trace metals basis
Sigma-Aldrich
羟基磷灰石, Type I, buffered aqueous suspension
Sigma-Aldrich
钛, nanoparticles, dispersion, <100 nm particle size, in mineral oil, 98.5% trace metals basis
Sigma-Aldrich
钛, foil, thickness 2.0 mm, 99.7% trace metals basis
Sigma-Aldrich
钛, foil, thickness 0.1 mm, 99.99% trace metals basis
Sigma-Aldrich
钛, crystalline, 5-10 mm, ≥99.99% trace metals basis (purity exclusive of Na and K content)
Sigma-Aldrich
钛, foil, thickness 0.5 mm, 99.99% trace metals basis
Sigma-Aldrich
钛, sputtering target, diam. × thickness 2.00 in. × 0.25 in., 99.995% trace metals basis
Sigma-Aldrich
钛, wire, diam. 0.81 mm, 99.7% trace metals basis
Sigma-Aldrich
钛, foil, thickness 0.25 mm, 99.99% trace metals basis
Sigma-Aldrich
钛, rod, diam. 6.35 mm, 99.99% trace metals basis
Sigma-Aldrich
钛, foil, thickness 0.127 mm, ≥99.99% trace metals basis
Sigma-Aldrich
钛, wire, diam. 1.0 mm, 99.99% trace metals basis
Sigma-Aldrich
钛, sputtering target, diam. × thickness 3.00 in. × 0.125 in., 99.995% trace metals basis
Sigma-Aldrich
钛, wire, diam. 0.5 mm, 99.99% trace metals basis
Sigma-Aldrich
钛, wire, diam. 2.0 mm, 99.99% trace metals basis
Sigma-Aldrich
钛, wire, diam. 0.127 mm, 99.99% trace metals basis
Sigma-Aldrich
钛, evaporation slug, diam. × L 6.3 mm × 6.3 mm, ≥99.99% trace metals basis
钛, IRMM®, certified reference material, 0.5 mm wire
钛, IRMM®, certified reference material, 0.1 mm foil
钛, IRMM®, certified reference material, 0.5 mm foil