  • Functionalized bio-artifact fabricated via selective slurry extrusion. Part 2: Fabrication of ceramic dental crown.

Functionalized bio-artifact fabricated via selective slurry extrusion. Part 2: Fabrication of ceramic dental crown.

Journal of nanoscience and nanotechnology (2014-04-17)
D B Zhu, J P Liang, Y X Qu, G L Duan
摘要

Functionalized ceramic dental crown was successfully fabricated through selective slurry extrusion (SSE) based technique of solid freeform fabrication (also known as rapid prototyping). After sintering, the decomposed tourmaline powders were embedded in ZrO2 matrix. The far infrared emission properties of the ceramic dental crown were improved due to the increase of the numbers of infrared active bonds from tourmaline. This new dental restoration process presents potential to provide dental patients with functionalized artificial teeth, which benefits the body health by the way of emitting far infrared rays in ambient temperatures.

材料
货号
品牌
产品描述

Sigma-Aldrich
氧化锆 (IV), powder, 5 μm, 99% trace metals basis
Sigma-Aldrich
氧化锆 (IV), nanopowder, <100 nm particle size (TEM)
Sigma-Aldrich
锆, powder, −100 mesh
Sigma-Aldrich
锆, foil, thickness 0.1 mm, 99.98% trace metals basis
Sigma-Aldrich
氧化锆 (IV), 99.99% trace metals basis (purity excludes ~2% HfO2)
Sigma-Aldrich
氧化锆(IV), nanoparticles, dispersion, <100 nm particle size (BET), 5 wt. % in H2O
Sigma-Aldrich
锆, sponge, ≥99% trace metals basis
Sigma-Aldrich
锆, rod, diam. 6.35 mm, ≥99% trace metals basis
Sigma-Aldrich
氧化锆(IV), nanoparticles, dispersion, <100 nm particle size (BET), 10 wt. % in H2O
锆, rod, 100mm, diameter 50mm, centerless ground, 99.2%
Sigma-Aldrich
锆, powder, in water, -325 mesh, 99.5% trace metals basis (excluding Hf)
锆, foil, not light tested, 50x50mm, thickness 0.006mm, 99.2%
锆, rod, 1000mm, diameter 1.5mm, 99.2%
锆, rod, 1000mm, diameter 12.7mm, centerless ground, 99.2%
锆, rod, 1000mm, diameter 2.0mm, centerless ground, 99.2%
锆, rod, 1000mm, diameter 3.0mm, centerless ground, 99.2%
锆, rod, 1000mm, diameter 5.0mm, centerless ground, 99.2%
锆, rod, 1000mm, diameter 6.0mm, centerless ground, 99.2%
锆, rod, 1000mm, diameter 9.5mm, centerless ground, 99.2%
锆, rod, 100mm, diameter 1.5mm, 99.2%
锆, rod, 100mm, diameter 12.7mm, centerless ground, 99.2%
锆, rod, 100mm, diameter 19.0mm, centerless ground, 99.2%
锆, rod, 100mm, diameter 2.0mm, centerless ground, 99.2%
锆, rod, 100mm, diameter 3.0mm, centerless ground, 99.2%
锆, rod, 100mm, diameter 5.0mm, centerless ground, 99.2%
锆, rod, 100mm, diameter 6.0mm, centerless ground, 99.2%
锆, rod, 100mm, diameter 9.5mm, centerless ground, 99.2%
锆, rod, 200mm, diameter 1.5mm, 99.2%
锆, rod, 200mm, diameter 12.7mm, centerless ground, 99.2%
锆, rod, 200mm, diameter 19.0mm, centerless ground, 99.2%

社交媒体

LinkedIn icon
Twitter icon
Facebook Icon
Instagram Icon

Merck

科研、开发、生产。

作为生命科学行业的全球领先供应商,我们致力于为科研、生物技术开发和生产,以及制药药物疗法开发和生产提供各类解决方案和服务。

© 2021年版权归德国达姆施塔特默克集团(Merck KGaA)及/或其附属公司所有。版权所有。

未经许可,严禁复制本网站上的任何资料。