  • Adhesive strength of the luting technique for passively fitting screw-retained implant-supported prostheses: an in vitro evaluation.

Adhesive strength of the luting technique for passively fitting screw-retained implant-supported prostheses: an in vitro evaluation.

The International journal of prosthodontics (2015-01-15)
Maria Menini, Francesco Pera, Marco Migliorati, Paolo Pesce, Paolo Pera
摘要

This in vitro study evaluated the adhesive strength of a technique to lute implant cylinders to metal frameworks in implant-supported prostheses and ensure a good passive fit. Different height samples were tested: In group 1, implant cylinders were 5 mm long; in group 2, they were 10 mm long. A universal testing machine (Instron) was used to perform pullout tests. The luting technique provided enough adhesive strength for clinical use with greater adhesive strength in group 2 (mean pull-out strength: 2.85 kN in group 1 versus 3.79 kN in group 2). The luting technique provides enough adhesive strength for clinical use. Moreover, specimens with a larger surface for adhesion demonstrated higher adhesive strength compared with shorter specimens.

材料
货号
品牌
产品描述

Sigma-Aldrich
钛, foil, thickness 0.127 mm, 99.7% trace metals basis
Sigma-Aldrich
钛, powder, <45 μm avg. part. size, 99.98% trace metals basis
Sigma-Aldrich
钛, foil, thickness 0.25 mm, 99.7% trace metals basis
Sigma-Aldrich
钛, powder, −100 mesh, 99.7% trace metals basis
Sigma-Aldrich
钛, foil, thickness 0.025 mm, 99.98% trace metals basis
Sigma-Aldrich
钛, sponge, 3-19 mm, 99.5% trace metals basis
Sigma-Aldrich
钛, wire, diam. 0.25 mm, 99.7% trace metals basis
Sigma-Aldrich
钛, nanoparticles, dispersion, <100 nm particle size, in mineral oil, 98.5% trace metals basis
Sigma-Aldrich
钛, sputtering target, diam. × thickness 2.00 in. × 0.25 in., 99.995% trace metals basis
Sigma-Aldrich
钛, foil, thickness 0.5 mm, 99.99% trace metals basis
Sigma-Aldrich
钛, wire, diam. 0.81 mm, 99.7% trace metals basis
Sigma-Aldrich
钛, foil, thickness 0.25 mm, 99.99% trace metals basis
Sigma-Aldrich
钛, foil, thickness 2.0 mm, 99.7% trace metals basis
Sigma-Aldrich
钛, wire, diam. 1.0 mm, 99.99% trace metals basis
Sigma-Aldrich
钛, evaporation slug, diam. × L 6.3 mm × 6.3 mm, ≥99.99% trace metals basis
Sigma-Aldrich
钛, foil, thickness 0.127 mm, ≥99.99% trace metals basis
Sigma-Aldrich
钛, wire, diam. 0.5 mm, 99.99% trace metals basis
Sigma-Aldrich
钛, wire, diam. 2.0 mm, 99.99% trace metals basis
钛, mesh, 150x150mm, nominal aperture 0.19mm, wire diameter 0.23mm, 60x60 wires/inch, open area 20%, twill weave
钛, rod, 100mm, diameter 2mm, annealed, 99.6+%
钛, IRMM®, certified reference material, 0.5 mm wire
钛, rod, 100mm, diameter 10mm, annealed, 99.6+%
Sigma-Aldrich
钛, wire, diam. 0.127 mm, 99.99% trace metals basis
钛, wire reel, 10m, diameter 0.75mm, as drawn, 99.6+%
钛, rod, 500mm, diameter 2mm, as drawn, 99.99+%
钛, wire reel, 1m, diameter 0.5mm, as drawn, 99.6+%
钛, tube, 500mm, outside diameter 0.51mm, inside diameter 0.35mm, wall thickness 0.08mm, annealed, 99.6+%
钛, tube, 500mm, outside diameter 0.81mm, inside diameter 0.61mm, wall thickness 0.1mm, as drawn, 99.6+%
钛, tube, 500mm, outside diameter 1.05mm, inside diameter 0.75mm, wall thickness 0.15mm, annealed, 99.6+%
钛, tube, 500mm, outside diameter 1.6mm, inside diameter 1.2mm, wall thickness 0.2mm, hard, 99.6+%