  • Lithium diffusivity in antimony-based intermetallic and FeSb-TiC composite anodes as measured by GITT.

Lithium diffusivity in antimony-based intermetallic and FeSb-TiC composite anodes as measured by GITT.

Physical chemistry chemical physics : PCCP (2015-10-10)
Eric Allcorn, Sang Ok Kim, Arumugam Manthiram
摘要

The diffusion coefficient of lithium is an important parameter in determining the rate capability of an electrode and its ability to deliver high power output. Galvanostatic intermittent titration technique (GITT) is a quick electrochemical method to determine diffusion coefficients in electrode materials and is applied here to antimony-based anodes for lithium-ion batteries. Like other alloy anodes, antimony suffers from large volume change and a short cycle life, so GITT is also applied to determine the effects on lithium diffusivity of antimony intermetallics and composite electrodes designed to mitigate these issues. Pure antimony is measured to have a diffusion coefficient of 4.0 × 10(-9) cm(2) s(-1), in agreement with previously measured values. The intermetallics NiSb, FeSb, and FeSb2 all demonstrate diffusivity values within an order of magnitude of antimony, while Cu2Sb shows roughly an order of magnitude improvement due to the persistence of the Cu2Sb phase during cycling. The composite electrode FeSb-TiC is shown to offer significant enhancement of the diffusion coefficient positively correlated with higher concentrations of TiC in the composite up to a maximum value of 1.9 × 10(-7) cm(2) s(-1) at 60 wt% TiC, nearly two full orders of magnitude greater than that of pure antimony.

材料
货号
品牌
产品描述

Sigma-Aldrich
1-甲基-2-吡咯烷酮, anhydrous, 99.5%
Sigma-Aldrich
1-甲基-2-吡咯烷酮, ACS reagent, ≥99.0%
Sigma-Aldrich
1-甲基-2-吡咯烷酮, ReagentPlus®, 99%
Sigma-Aldrich
1-甲基-2-吡咯烷酮, biotech. grade, ≥99.7%
Sigma-Aldrich
锑, powder, -100 mesh, 99.5% trace metals basis
Sigma-Aldrich
锑, beads, 1-5 mm, low oxide, 99.999% trace metals basis
锑, rod, 20mm, diameter 4.7mm, 99.999%
锑, rod, 6mm, diameter 6mm, 99.999%
锑, foil, 50x50mm, thickness 2mm, hot-pressed
锑, foil, light tested, 25x25mm, thickness 0.05mm, permanent polyester support, 95+%
锑, foil, light tested, 50x50mm, thickness 0.05mm, permanent polyester support, 95+%
锑, foil, not light tested, 100x100mm, thickness 0.015mm, permanent polyester support, 95+%
锑, foil, not light tested, 100x100mm, thickness 0.01mm, permanent polyester support, 95+%
锑, foil, not light tested, 100x100mm, thickness 0.025mm, permanent polyester support, 95+%
锑, foil, not light tested, 100x100mm, thickness 0.05mm, permanent polyester support, 95+%
锑, foil, not light tested, 25x25mm, thickness 0.002mm, permanent polyester support, 95+%
锑, foil, not light tested, 25x25mm, thickness 0.005mm, permanent polyester support, 95+%
锑, foil, not light tested, 25x25mm, thickness 0.015mm, permanent polyester support, 95+%
锑, foil, not light tested, 25x25mm, thickness 0.025mm, permanent polyester support, 95+%
锑, foil, not light tested, 50x50mm, thickness 0.002mm, permanent polyester support, 95+%
锑, foil, not light tested, 50x50mm, thickness 0.005mm, permanent polyester support, 95+%
锑, foil, not light tested, 50x50mm, thickness 0.015mm, permanent polyester support, 95+%
锑, foil, not light tested, 50x50mm, thickness 0.025mm, permanent polyester support, 95+%
锑, foil, not light tested, 50x50mm, thickness 0.05mm, permanent polyester support, 95+%
锑, microfoil, 25x25mm, thinness 0.5μm, specific density 334.5μg/cm2, 6 micron aluminum permanent support, 95+%
锑, microfoil, 50x50mm, thinness 0.5μm, specific density 334.5μg/cm2, 6 micron aluminum permanent support, 95+%
锑, rod, 15mm, diameter 2.0mm, 99.99%
锑, rod, 25mm, diameter 2.0mm, 99.99%
锑, rod, 50mm, diameter 2.0mm, 99.99%
锑, rod, 50mm, diameter 4.7mm, 99.999%

社交媒体

LinkedIn icon
Twitter icon
Facebook Icon
Instagram Icon

Merck

科研、开发、生产。

作为生命科学行业的全球领先供应商,我们致力于为科研、生物技术开发和生产,以及制药药物疗法开发和生产提供各类解决方案和服务。

© 2021年版权归德国达姆施塔特默克集团(Merck KGaA)及/或其附属公司所有。版权所有。

未经许可,严禁复制本网站上的任何资料。