Electrodeposition of nanocrystalline Ni-W coatings with citric acid system.

Journal of nanoscience and nanotechnology (2013-05-08)
Jingjing Du, Lijian Xu, Baizhen Chen, Li De
PMID23646798
RESUMEN

Ni-W alloy coatings were prepared by electrodeposition technique with citric acid as a complexing agent. The influence of the main technical parameters on W content in the Ni-W alloy coatings were investigated by electron dispersive spectroscopy (EDS), and the microstructure of the coatings was characterized and analyzed by employing X-ray diffractometer (XRD), scanning electron microscope (SEM). The results showed that bright and compact Ni-W alloy coatings with 25.78 wt% W were obtained when the concentration of Na2WO4 x 2H2O was 50 g/L, the concentration of NH4Cl was 20 g/L, the bath pH value was 8.0 and the bath temperature was 70 degrees C. The surface of Ni-W alloy coatings were bright, flat and compact, the mircostructure of the alloy coatings were nanocrystalline and the average grain size was about 38 nm by calculating using Scherrer Equation.

MATERIALES
Referencia del producto
Marca
Descripción del producto
268259
Sigma-Aldrich
Nickel, foil, thickness 0.125 mm, ≥99.9%
357189
Sigma-Aldrich
Tungsten, foil, thickness 0.5 mm, ≥99.9% trace metals basis
267554
Sigma-Aldrich
Tungsten, wire, diam. 0.25 mm, ≥99.9% trace metals basis
267562
Sigma-Aldrich
Tungsten, wire, diam. 1.0 mm, 99.99% trace metals basis
510068
Sigma-Aldrich
Raney®-Nickel, W.R. Grace and Co. Raney® 3202, slurry, in H2O, active catalyst
510033
Sigma-Aldrich
Raney®-Nickel, W.R. Grace and Co. Raney® 2400, slurry, in H2O, active catalyst
C2404
Sigma-Aldrich
Citric acid, anhydrous, suitable for cell culture, suitable for plant cell culture
357197
Sigma-Aldrich
Tungsten, foil, thickness 0.127 mm, ≥99.9% trace metals basis
221678
Sigma-Aldrich
Raney®-Nickel, W.R. Grace and Co. Raney® 2800, slurry, in H2O, active catalyst
W230618
Sigma-Aldrich
Citric acid, ≥99.5%, FCC, FG
27487
Sigma-Aldrich
Citric acid, BioUltra, anhydrous, ≥99.5% (T)
C0759
Sigma-Aldrich
Citric acid, 99%
203904
Sigma-Aldrich
Nickel, powder, <150 μm, 99.99% trace metals basis
510041
Sigma-Aldrich
Raney®-Nickel, W.R. Grace and Co. Raney® 4200, slurry, in H2O, active catalyst
356972
Sigma-Aldrich
Tungsten, wire, diam. 0.5 mm, ≥99.9% trace metals basis
267007
Sigma-Aldrich
Nickel, foil, thickness 0.25 mm, 99.995% trace metals basis
267058
Sigma-Aldrich
Nickel, wire, diam. 0.5 mm, ≥99.99% trace metals basis
268283
Sigma-Aldrich
Nickel, powder, <1 μm, 99.8% trace metals basis
46933
Supelco
Citric acid, analytical standard
357634
Sigma-Aldrich
Nickel, wire, diam. 0.25 mm, ≥99.9%
251275
Sigma-Aldrich
Citric acid, ACS reagent, ≥99.5%
357421
Sigma-Aldrich
Tungsten, powder, 10 μm, ≥99.99% trace metals basis
767484
Sigma-Aldrich
Nickel, sputtering target, diam. × thickness 2.00 in. × 0.25 in., 99.95% trace metals basis
PHR1071
Supelco
Citric acid, Anhydrous, Pharmaceutical Secondary Standard; Certified Reference Material
94676
Supelco
Citric acid, certified reference material, TraceCERT®
27109
Sigma-Aldrich
Citric acid, meets analytical specification of Ph. Eur., BP, USP, E330, anhydrous, 99.5-100.5% (based on anhydrous substance)
357626
Sigma-Aldrich
Nickel, wire, diam. 0.5 mm, ≥99.9% trace metals basis
357588
Sigma-Aldrich
Nickel, foil, thickness 0.1 mm, 99.98% trace metals basis
357553
Sigma-Aldrich
Nickel, foil, thickness 0.5 mm, 99.98% trace metals basis
510106
Sigma-Aldrich
Tungsten, powder (monocrystalline), 0.6-1 μm, ≥99.9% trace metals basis