Hydrothermal synthesis of tetragonal BaTiO3 nanotube arrays with high dielectric performance.

Hydrothermal synthesis of tetragonal BaTiO3 nanotube arrays with high dielectric performance.

Journal of nanoscience and nanotechnology (2014-04-18)

Liming Wang, Xiangyun Deng, Jianbao Li, Xinxing Liao, Guoqing Zhang, Chunpeng Wang, Kuifan Su

ABSTRACT

Tetragonal Barium titanate (BaTiO3) nanotube arrays have been prepared using the template-assisted hydrothermal method combined with an annealing process. The in-situ chemical conversion of TiO2 nanotube array templates ensured that BaTiO3 maintained the morphology of the nanotube architectures. Moreover, X-ray diffraction and Raman spectrum characterization were used to confirm that the BaTiO3 nanotube arrays had a tetragonal phase after the use of a simple annealing technique. Typical hysteresis loops showed their ferroelectricity, with the remanent polarization and coercive fields being 2.57 microC/cm2 and 2.52 kV/cm, respectively. The relative dielectric constant of the tetragonal BaTiO3 nanotube arrays reached up to 1000 and the dielectric loss was as low as 0.02 at 1 kHz at room temperature.

MATERIALS

Product Number

Brand

Product Description

266035

Sigma-Aldrich

Titanium, wire, diam. 1.0 mm, 99.99% trace metals basis

369489

Sigma-Aldrich

Titanium, foil, thickness 2.0 mm, 99.7% trace metals basis

208108

Sigma-Aldrich

Barium titanate(IV), powder, <3 μm, 99%

267902

Sigma-Aldrich

Titanium, wire, diam. 0.81 mm, 99.7% trace metals basis

IRMM531C

Titanium, IRMM^®, certified reference material, 0.5 mm wire

IRMM531B

Titanium, IRMM^®, certified reference material, 0.5 mm foil

467634

Sigma-Aldrich

Barium titanate(IV), nanopowder (cubic crystalline phase), <100 nm particle size (BET), ≥99% trace metals basis

348848

Sigma-Aldrich

Titanium, foil, thickness 0.025 mm, 99.98% trace metals basis

348791

Sigma-Aldrich

Titanium, foil, thickness 0.127 mm, 99.7% trace metals basis

338842

Sigma-Aldrich

Barium titanate(IV), powder, <2 μm, 99.5% trace metals basis

460400

Sigma-Aldrich

Titanium, wire, diam. 0.25 mm, 99.7% trace metals basis

305812

Sigma-Aldrich

Titanium, ≤10 mm, ≥99.99% trace metals basis (purity exclusive of Na and K content)

GF06082286

Titanium, microfoil, disks, 10mm, thinness 1.0μm, specific density 429μg/cm², permanent mylar 3.5μm support, 99.6+%

GF17705516

Titanium, rod, 200mm, diameter 3.0mm, annealed, 99.6+%

GF12929744

Titanium, microfoil, disks, 25mm, thinness 0.25μm, specific density 112.6μg/cm², permanent mylar 3.5μm support, 99.6+%

GF54883581

Titanium, rod, 1000mm, diameter 3.0mm, annealed, 99.6+%

GF16031843

Titanium, mesh, 100x100mm, nominal aperture 0.19mm, wire diameter 0.23mm, 60x60 wires/inch, open area 20%, twill weave

GF61322699

Titanium, rod, 100mm, diameter 2mm, annealed, 99.6+%

GF04311638

Titanium, rod, 100mm, diameter 6mm, annealed, 99.6+%

GF91859967

Titanium, rod, 100mm, diameter 9.5mm, annealed, 99.99+%

GF66991179

Titanium, rod, 100mm, diameter 2mm, as drawn, 99.99+%

GF24976525

Titanium, rod, 200mm, diameter 25mm, annealed, 99.6+%

745952

Sigma-Aldrich

Barium titanate(IV), nanopowder (cubic), 50 nm (SEM), 99.9% trace metals basis

GF16213553

Titanium, wire reel, 10m, diameter 0.125mm, annealed, 99.6+%

GF26602321

Titanium, tube, 500mm, outside diameter 25.4mm, inside diameter 23.62mm, wall thickness 0.89mm, annealed, 99.6+%

GF56868766

Titanium, wire reel, 25m, diameter 1.0mm, annealed, 99.6+%

GF61228403

Titanium, wire reel, 50m, diameter 0.75mm, as drawn, 99.6+%

GF36425707

Titanium, wire reel, 200m, diameter 0.20mm, annealed, 99.6+%

GF14377631

Titanium, wire reel, 25m, diameter 0.25mm, annealed, 99.6+%

GF55775975

Titanium, wire reel, 25m, diameter 0.25mm, as drawn, 99.6+%