  • Fabrication of zero valent iron (ZVI) nanotube film via potentiostatic anodization and electroreduction.

Fabrication of zero valent iron (ZVI) nanotube film via potentiostatic anodization and electroreduction.

Water science and technology : a journal of the International Association on Water Pollution Research (2009-06-23)
Jun-Won Jang, Jung-Eui Jun, Jae-Woo Park
ABSTRACT

Zero valent iron has been successfully used for the degradation of a wide range of contaminants. However, this reaction of using ZVI particle produces a large quantity of iron sludge. To solve the problem, we report the synthesis of self-organized nanoporous zero valent iron film treated with anodization and electro-reduction of iron foil. The iron nanotubes were fabricated in 1 M Na(2)SO(4) + 0.5 wt% NaF electrolyte by supplying constant electric currents of 50 mV/s, and holding the potential at 20, 40 and 60 V for 20 min. Nanoporous shape was produced by anodic oxidation of iron film. After anodizing process, electro-reduction of nanoporous iron film converted crystallization iron oxide to zero valent iron. Electro-reduction process was carried out by electro-reducing with powersupply to and holding the potential at 20 V for 20 min. The surface of iron nanotube film was examined by BET and the thickness of the oxidized films was evaluated by scanning electron microscope (SEM). The crystalline structures of the fabricated films were evaluated using X-ray diffraction (XRD).

MATERIALS
Product Number
Brand
Product Description

Iron, foil, 300x300mm, thickness 0.1mm, hard, 99.5%
Iron, foil, 0.2m coil, thickness 0.5mm, coil width 49mm, armco« soft ingot 99.8+%
Iron, foil, 10mm disks, thickness 0.01mm, 99.85%
Iron, foil, 10mm disks, thickness 0.01mm, 99.99+%
Iron, foil, 10mm disks, thickness 0.020mm, 99.85%
Iron, foil, 10mm disks, thickness 0.025mm, as rolled, 99.99+%
Iron, foil, 10mm disks, thickness 0.025mm, hard, 99.5%
Iron, foil, 10mm disks, thickness 0.038mm, hard, 99.5%
Iron, foil, 10mm disks, thickness 0.05mm, as rolled, 99.99+%
Iron, foil, 10mm disks, thickness 0.05mm, hard, 99.5%
Iron, foil, 10mm disks, thickness 0.075mm, as rolled, 99.99+%
Iron, foil, 10mm disks, thickness 0.075mm, hard, 99.5%
Iron, foil, 10mm disks, thickness 0.125mm, as rolled, 99.99+%
Iron, foil, 10mm disks, thickness 0.125mm, hard, 99.5%
Iron, foil, 10mm disks, thickness 0.15mm, hard, 99.5%
Iron, foil, 10mm disks, thickness 0.1mm, hard, 99.5%
Iron, foil, 10mm disks, thickness 0.20mm, hard, 99.5%
Iron, foil, 10mm disks, thickness 0.25mm, as rolled, 99.99+%
Iron, foil, 10mm disks, thickness 0.25mm, hard, 99.5%
Iron, foil, 10mm disks, thickness 0.38mm, hard, 99.5%
Iron, foil, 10mm disks, thickness 0.5mm, as rolled, 99.99+%
Iron, foil, 10mm disks, thickness 0.5mm, hard, 99.5%
Iron, foil, 10mm disks, thickness 0.9mm, as rolled, 99.5%
Iron, foil, 10mm disks, thickness 1.0mm, as rolled, 99.5%
Iron, foil, 15mm disks, thickness 0.003mm, 99.85%
Iron, foil, 15mm disks, thickness 0.004mm, 99.85%
Iron, foil, 15mm disks, thickness 0.004mm, 99.99+%
Iron, foil, 15mm disks, thickness 0.005mm, 99.85%
Iron, foil, 15mm disks, thickness 0.006mm, 99.85%
Iron, foil, 15mm disks, thickness 0.007mm, 99.85%

Social Media

LinkedIn icon
Twitter icon
Facebook Icon
Instagram Icon

Merck

Research. Development. Production.

We are a leading supplier to the global Life Science industry with solutions and services for research, biotechnology development and production, and pharmaceutical drug therapy development and production.

© 2021 Merck KGaA, Darmstadt, Germany and/or its affiliates. All Rights Reserved.

Reproduction of any materials from the site is strictly forbidden without permission.