  • Enhanced electrochromic coloration of poly(3-hexylthiophene) films by electrodeposited Au nanoparticles.

Enhanced electrochromic coloration of poly(3-hexylthiophene) films by electrodeposited Au nanoparticles.

Journal of nanoscience and nanotechnology (2013-07-19)
Yoon-Chae Nah
摘要

Au nanoparticles and poly(3-hexylthiophene) (P3HT) composite films were prepared by electrodeposition of Au nanoparticles using pulse-current electrodeposition followed by the spin coating of P3HT and their enhanced electrochromic coloration was investigated. A relatively uniformed Au nanoparticle was obtained by the controlled electrodeposition on indium tin oxide (ITO) substrate and plasmon absorption band of Au nanoparticles were observed. Optical and electrochemical properties of Au/P3HT composite films were compared with the pure P3HT films. The enhanced electrochromic absorption of the composite films was observed due to the surface plasmon resonance of the Au nanoparticles.

材料
货号
品牌
产品描述

Sigma-Aldrich
金, wire, diam. 0.25 mm, ≥99.9% trace metals basis
Sigma-Aldrich
金, nanopowder, <100 nm particle size, 99.9% trace metals basis
Sigma-Aldrich
金, foil, thickness 0.127 mm, 99.99% trace metals basis
Sigma-Aldrich
镀金显微镜载片, layer thickness 100 Å, 99.999% (Au)
Sigma-Aldrich
金, powder, <45 μm, 99.99% trace metals basis
Sigma-Aldrich
金, wire, diam. 0.5 mm, 99.99% trace metals basis
Sigma-Aldrich
金, foil, thickness 0.5 mm, 99.99% trace metals basis
Sigma-Aldrich
镀金显微镜载片, layer thickness 1000 Å, 99.999% (Au)
Sigma-Aldrich
金, beads, 1-6 mm, 99.999% trace metals basis
Sigma-Aldrich
金, foil, thickness 0.025 mm, 99.99% trace metals basis
Sigma-Aldrich
金, wire, diam. 0.1 mm, 99.99% trace metals basis
Sigma-Aldrich
金, wire, diam. 0.5 mm, 99.999% trace metals basis
Sigma-Aldrich
金, foil, thickness 0.1 mm, 99.99% trace metals basis
Sigma-Aldrich
金, wire, diam. 1.0 mm, 99.99% trace metals basis
Sigma-Aldrich
金, powder, <10 μm, ≥99.9% trace metals basis
Sigma-Aldrich
金, evaporation slug, diam. × L 0.3 cm × 0.6 cm, 99.99% trace metals basis
Sigma-Aldrich
金, wire, diam. 1.0 mm, 99.997% trace metals basis
Sigma-Aldrich
金, foil, thickness 0.25 mm, ≥99.9% trace metals basis
Sigma-Aldrich
金, powder, <850 μm, ≥99.99% trace metals basis
Sigma-Aldrich
金, wire, diam. 0.25 mm, 99.99% trace metals basis
Sigma-Aldrich
金, foil, thickness 0.05 mm, 99.99% trace metals basis
Sigma-Aldrich
金, wire, diam. 0.127 mm, 99.99% trace metals basis
Sigma-Aldrich
镀金盖玻片, 99.999% (Au), diam. × thickness 15 mm × 130-170 μm, layer thickness 100 Å
Sigma-Aldrich
镀金盖玻片, L × W × thickness 22 mm × 22 mm × 130-170 μm, square, 99.999% (Au), layer thickness 100 Å
Sigma-Aldrich
金, wire, diam. 2.0 mm, 99.99% trace metals basis
Sigma-Aldrich
金, rod, diam. 3.0 mm, 99.99% trace metals basis
Sigma-Aldrich
金, evaporation slug, diam. × L 0.6 cm × 1.2 cm, 99.99% trace metals basis
Sigma-Aldrich
金, wire, diam. 1.5 mm, 99.999% trace metals basis