  • Preparation and thermoelectric properties of Ag-dispersed Bi0.5Sb1.5Te3.

Preparation and thermoelectric properties of Ag-dispersed Bi0.5Sb1.5Te3.

Journal of nanoscience and nanotechnology (2013-07-19)
Ii-Ho Kim, Soon-Mok Choi, Won-Seon Sea, Dong-Ik Cheong
摘要

Ag-dispersed Bi0.5Sb1.5Te3 was prepared successfully by silver acetate (AgOAc) decomposition and hot pressing. The Ag nanoparticles were well-dispersed in the Bi0.5Sb1.5Te3 matrix, and acted as phonon scattering centers effectively. The electrical conductivity increased systematically with increasing amount of Ag nanoparticle dispersion, whereas it decreased with increasing temperature similar to metals or degenerate semiconductors. All specimens had a positive Seebeck coefficient, which confirmed that the electrical charge was transported mainly by holes. The Seebeck coefficient of Bi0.5Sb1.5Te3 decreased with increasing temperature but its temperature dependence was changed by Ag dispersion. The power factor values for Ag-dispersed Bi0.5Sb1.5Te3 increased significantly due to the increase in effective carrier mass and were higher over the entire temperature range. The decrease in lattice thermal conductivity by Ag dispersion overcame the increase in electronic thermal conductivity. The thermoelectric figure of merit was enhanced remarkably over a wide temperature range of 323-523 K due to the high power factor and the maintenance of low thermal conductivity.

材料
货号
品牌
产品描述

Sigma-Aldrich
银, conductive paste
Sigma-Aldrich
银, nanopowder, <100 nm particle size, contains PVP as dispersant, 99.5% trace metals basis
Sigma-Aldrich
银纳米线悬浮液, diam. × L 60 nm × 10 μm, 0.5% (isopropyl alcohol suspension)
Sigma-Aldrich
银, powder, 2-3.5 μm, ≥99.9% trace metals basis
Sigma-Aldrich
银, wire, diam. 0.5 mm, 99.9% trace metals basis
Sigma-Aldrich
银, flakes, 10 μm, ≥99.9% trace metals basis
Sigma-Aldrich
银, nanopowder, <150 nm particle size, 99% trace metals basis
Sigma-Aldrich
银, powder, 5-8 μm, ≥99.9% trace metals basis
Sigma-Aldrich
银, wire, diam. 0.25 mm, ≥99.99% trace metals basis
Sigma-Aldrich
银, wire, diam. 1.0 mm, 99.9% trace metals basis
Sigma-Aldrich
银, wire, diam. 0.5 mm, ≥99.99% trace metals basis
Sigma-Aldrich
银, foil, thickness 0.1 mm, 99.9% trace metals basis
Sigma-Aldrich
银, shot, 1-3 mm, ≥99.99% trace metals basis
Sigma-Aldrich
银, foil, thickness 0.25 mm, 99.9% trace metals basis
Sigma-Aldrich
银, foil, thickness 0.025 mm, 99.9% trace metals basis
Sigma-Aldrich
银纳米线悬浮液, diam. × L 115 nm × 20-50 μm, 0.5% (isopropyl alcohol suspension)
Sigma-Aldrich
银, granular, >250 μm, 99.99% trace metals basis
Sigma-Aldrich
银, powder, <45 μm, ≥99.99% trace metals basis
Sigma-Aldrich
银, powder, <250 μm, 99.99% trace metals basis
Sigma-Aldrich
银, foil, thickness 1.0 mm, 99.99% trace metals basis
Sigma-Aldrich
银, wire, diam. 0.1 mm, 99.9% trace metals basis
Sigma-Aldrich
银, foil, thickness 0.5 mm, 99.99% trace metals basis
Sigma-Aldrich
银, wire, diam. 0.25 mm, 99.9% trace metals basis
Sigma-Aldrich
银, wool, diam. 0.05 mm, ≥99.9% trace metals basis
Sigma-Aldrich
银, wire, diam. 1.0 mm, ≥99.99% trace metals basis
Sigma-Aldrich
银, evaporation slug, diam. × L 0.6 cm × 1.2 cm, 99.99% trace metals basis
Sigma-Aldrich
银, wire, diam. 2.0 mm, ≥99.99% trace metals basis
Sigma-Aldrich
银, foil, thickness 1.5 mm, 99.9% trace metals basis
Sigma-Aldrich
银, foil, thickness 0.5 mm, 99.9% trace metals basis
Sigma-Aldrich
银, rod, diam. 7.0 mm, 99.99% trace metals basis