  • Anodic TiO2 nanotubular arrays with pre-synthesized hydroxyapatite--an effective approach to enhance the biocompatibility of titanium.

Anodic TiO2 nanotubular arrays with pre-synthesized hydroxyapatite--an effective approach to enhance the biocompatibility of titanium.

Journal of nanoscience and nanotechnology (2013-07-26)
Lu-Ning Wang, Long-Xiang Lin, Chang-Jian Lin, Chen Shen, Alyssa Shinbine, Jing-Li Luo
ABSTRACT

Electrochemically anodized TiO2 nanotubular arrays can provide large surface areas for biological species attachment. In order to further enhance the biocompatibility of Ti medical implants, we deposited a pre-synthesized hydroxyapatite inside and on the nanotubular arrays, and examined the biocompatibility of the anodized TiO2 nanotubular arrays with pre-synthesized hydroxyapatite by in vitro assessment in simulated body fluid, and in vitro cell culture. The results showed that the hydroxyapatite coating was able to be induced on TiO2 nanotubular arrays with pre-synthesized hydroxyapatite within 5 days while only a thin film composed of calcium phosphorous chemicals formed on as-formed TiO2 nanotubular arrays. The cell culture evaluation further proved the enhancement of cell attachment and proliferation on TiO2 nanotubular arrays with pre-synthesized hydroxyapatite as opposed to those without pre-synthesized hydroxyapatite. The present study proves that formation of TiO2 nanotubular arrays with pre-synthesized hydroxyapatite a promising method to enhance the biocompatibility of Ti implants.

MATERIALS
Product Number
Brand
Product Description

Sigma-Aldrich
氧化钛 (IV),锐钛矿, nanopowder, <25 nm particle size, 99.7% trace metals basis
Sigma-Aldrich
二氧化钛(IV), nanopowder, 21 nm primary particle size (TEM), ≥99.5% trace metals basis
Sigma-Aldrich
氧化钛 (IV),锐钛矿, powder, 99.8% trace metals basis
Sigma-Aldrich
钛 (IV) 氧化物,金红石型, powder, <5 μm, ≥99.9% trace metals basis
Sigma-Aldrich
钛 (IV) 氧化物,金红石型, nanopowder, <100 nm particle size, 99.5% trace metals basis
Sigma-Aldrich
氧化钛 (IV),锐钛矿, powder, −325 mesh, ≥99% trace metals basis
Sigma-Aldrich
二氧化钛(IV), ReagentPlus®, ≥99%
Sigma-Aldrich
氧化钛(IV),金红石和锐钛矿混合物, nanopowder, <100 nm particle size (BET), 99.5% trace metals basis
Sigma-Aldrich
二氧化钛(IV), puriss., meets analytical specification of Ph. Eur., BP, USP, 99-100.5%
Sigma-Aldrich
钛, foil, thickness 0.127 mm, 99.7% trace metals basis
Sigma-Aldrich
钛, powder, <45 μm avg. part. size, 99.98% trace metals basis
Sigma-Aldrich
羟基磷灰石, puriss., meets analytical specification of Ph. Eur., BP, FCC, E341, ≥90% (calculated on glowed substance)
Sigma-Aldrich
钛, foil, thickness 0.25 mm, 99.7% trace metals basis
Sigma-Aldrich
钛, powder, −100 mesh, 99.7% trace metals basis
Sigma-Aldrich
羟基磷灰石, Type I, buffered aqueous suspension
Sigma-Aldrich
氧化钛(IV),金红石和锐钛矿混合物, nanoparticles, <150 nm particle size (volume distribution, DLS), dispersion, 40 wt. % in H2O, 99.5% trace metals basis
Sigma-Aldrich
钛, foil, thickness 0.025 mm, 99.98% trace metals basis
Sigma-Aldrich
羟基磷灰石, purum p.a., ≥90% (as Ca3(PO4)2, KT)
Sigma-Aldrich
钛 (IV) 氧化物,金红石型, 99.995% trace metals basis
Sigma-Aldrich
钛, wire, diam. 0.25 mm, 99.7% trace metals basis
Sigma-Aldrich
氧化钛(IV),金红石和锐钛矿混合物, nanoparticle, <250 nm particle size (DLS), paste, 53-57 wt. % in diethylene glycol monobutyl ether/ethylene glycol, 99.9% trace metals basis
Sigma-Aldrich
钛 (IV) 氧化物,金红石型, ≥99.98% trace metals basis
Sigma-Aldrich
钛, foil, thickness 0.5 mm, 99.99% trace metals basis
Sigma-Aldrich
钛, crystalline, 5-10 mm, ≥99.99% trace metals basis (purity exclusive of Na and K content)
Sigma-Aldrich
钛, foil, thickness 0.1 mm, 99.99% trace metals basis
Sigma-Aldrich
钛, sponge, 3-19 mm, 99.5% trace metals basis
Sigma-Aldrich
钛, wire, diam. 0.81 mm, 99.7% trace metals basis
Sigma-Aldrich
钛, foil, thickness 2.0 mm, 99.7% trace metals basis
Sigma-Aldrich
二氧化钛(IV), contains 1% Mn as dopant, nanopowder, <100 nm particle size (BET), ≥97%
Sigma-Aldrich
钛, sputtering target, diam. × thickness 2.00 in. × 0.25 in., 99.995% trace metals basis