  • Low-temperature synthesis of graphene on nickel foil by microwave plasma chemical vapor deposition.

Low-temperature synthesis of graphene on nickel foil by microwave plasma chemical vapor deposition.

Applied physics letters (2011-07-30)
Y Kim, W Song, S Y Lee, C Jeon, W Jung, M Kim, C-Y Park
摘要

Microwave plasma chemical vapor deposition (MPCVD) was employed to synthesize high quality centimeter scale graphene film at low temperatures. Monolayer graphene was obtained by varying the gas mixing ratio of hydrogen and methane to 80:1. Using advantages of MPCVD, the synthesis temperature was decreased from 750 °C down to 450 °C. Optical microscopy and Raman mapping images exhibited that a large area monolayer graphene was synthesized regardless of the temperatures. Since the overall transparency of 89% and low sheet resistances ranging from 590 to 1855 Ω∕sq of graphene films were achieved at considerably low synthesis temperatures, MPCVD can be adopted in manufacturing future large-area electronic devices based on graphene film.

材料
货号
品牌
产品描述

镍, foil, 50x50mm, thickness 0.30mm, as rolled, 99.98%
镍, foil, light tested, 100x100mm, thickness 0.015mm, 99.9%
镍, foil, 10mm disks, thickness 0.15mm, annealed, 99%
镍, foil, 4mm disks, thickness 0.075mm, annealed, 99%
镍, foil, 4mm disks, thickness 0.075mm, as rolled, 99.98%
镍, foil, 4mm disks, thickness 0.125mm, annealed, 99%
镍, foil, 4mm disks, thickness 0.125mm, annealed, 99.98%
镍, foil, 4mm disks, thickness 0.125mm, as rolled, 100%
镍, foil, 4mm disks, thickness 0.125mm, as rolled, 99.99+%
镍, foil, 4mm disks, thickness 0.15mm, annealed, 99%
镍, foil, 4mm disks, thickness 0.1mm, annealed, 99%
镍, foil, 4mm disks, thickness 0.20mm, annealed, 99%
镍, foil, 4mm disks, thickness 0.25mm, annealed, 99%
镍, foil, 4mm disks, thickness 0.25mm, annealed, 99.98%
镍, foil, 4mm disks, thickness 0.25mm, as rolled, 100%
镍, foil, 4mm disks, thickness 0.25mm, as rolled, 99.99+%
镍, foil, 4mm disks, thickness 0.30mm, as rolled, 99.98%
镍, foil, 4mm disks, thickness 0.3mm, annealed, 99%
镍, foil, 4mm disks, thickness 0.3mm, as rolled, 100%
镍, foil, 4mm disks, thickness 0.50mm, annealed, 99%
镍, foil, 4mm disks, thickness 0.5mm, annealed, 99.98%
镍, foil, 4mm disks, thickness 0.5mm, as rolled, 100%
镍, foil, 4mm disks, thickness 0.5mm, as rolled, 99.99+%
镍, foil, 50mm disks, thickness 0.0025mm, 99.95%
镍, foil, 50mm disks, thickness 0.003mm, 99.95%
镍, foil, 50mm disks, thickness 0.005mm, as rolled, 99.9%
镍, foil, 50mm disks, thickness 0.0075mm, 99.9%
镍, foil, 50mm disks, thickness 0.0075mm, 99.95%
镍, foil, 50mm disks, thickness 0.0125mm, 99.9%
镍, foil, 50mm disks, thickness 0.0125mm, 99.99+%

社交媒体

LinkedIn icon
Twitter icon
Facebook Icon
Instagram Icon

Merck

科研、开发、生产。

作为生命科学行业的全球领先供应商,我们致力于为科研、生物技术开发和生产,以及制药药物疗法开发和生产提供各类解决方案和服务。

© 2021年版权归德国达姆施塔特默克集团(Merck KGaA)及/或其附属公司所有。版权所有。

未经许可,严禁复制本网站上的任何资料。