  • A multiscalar photoluminescence approach to discriminate among semiconducting historical zinc white pigments.

A multiscalar photoluminescence approach to discriminate among semiconducting historical zinc white pigments.

The Analyst (2013-04-05)
Loïc Bertrand, Matthieu Réfrégiers, Barbara Berrie, Jean-Philippe Échard, Mathieu Thoury
摘要

In order to fully characterize the zinc white artists' pigment (ZnO), much used since the mid-nineteenth century, three samples collected in the early 20th century were studied using a combination of synchrotron and macroscopic photoluminescence spectroscopy and imaging. An improved microscope setup based on synchrotron microspectroscopy and microimaging was used to study the powders dispersed onto indium foil. The synchrotron setup offered a diffraction-limited resolution of 153 nm. The PL spectra of individual grains were measured and the distribution of particles' emission spectra was mapped at the nanoscale. The results revealed that while the samples have apparent homogeneous photoluminescence behavior at the macroscale (bulk), their PL signatures are inhomogeneous below 20 μm. At the nanoscale the three powder samples have quite different PL signatures. Different sources, perhaps even different batches, of zinc white might be readily differentiated using this method.

材料
货号
品牌
产品描述

铟, foil, not light tested, 50x50mm, thickness 0.0025mm, temporary acrylic support, 99.8%
铟, foil, 100x100mm, thickness 0.25mm, as rolled, 99.999%
铟, foil, 50x50mm, thickness 0.5mm, as rolled, 99.999%
铟, foil, 6mm disks, thickness 0.1mm, as rolled, 100%
铟, foil, 6mm disks, thickness 0.20mm, as rolled, 100%
铟, foil, 6mm disks, thickness 0.25mm, as rolled, 100%
铟, foil, 6mm disks, thickness 0.5mm, as rolled, 100%
铟, foil, 6mm disks, thickness 0.75mm, as rolled, 100%
铟, foil, 6mm disks, thickness 1.0mm, as rolled, 100%
铟, foil, 8mm disks, thickness 0.0125mm, temporary acrylic support, 99.8%
铟, foil, 8mm disks, thickness 0.015mm, 99.8%
铟, foil, 8mm disks, thickness 0.01mm, 99.8%
铟, foil, 8mm disks, thickness 0.025mm, 99.8%
铟, foil, 8mm disks, thickness 0.02mm, 99.8%
铟, foil, 8mm disks, thickness 0.03mm, 99.8%
铟, foil, 8mm disks, thickness 0.04mm, 99.8%
铟, foil, 8mm disks, thickness 0.05mm, as rolled, 100%
铟, foil, 8mm disks, thickness 0.075mm, as rolled, 100%
铟, foil, 8mm disks, thickness 0.125mm, as rolled, 100%
铟, foil, 8mm disks, thickness 0.1mm, as rolled, 100%
铟, foil, 8mm disks, thickness 0.20mm, as rolled, 100%
铟, foil, 8mm disks, thickness 0.25mm, as rolled, 100%
铟, foil, 8mm disks, thickness 0.5mm, as rolled, 100%
铟, foil, 8mm disks, thickness 0.75mm, as rolled, 100%
铟, foil, 8mm disks, thickness 1.0mm, as rolled, 100%
铟, foil, light tested, 100x100mm, thickness 0.075mm, as rolled, 100%
铟, foil, light tested, 25x25mm, thickness 0.05mm, as rolled, 100%
铟, foil, light tested, 25x25mm, thickness 0.075mm, as rolled, 100%
铟, foil, light tested, 50x50mm, thickness 0.05mm, as rolled, 100%
铟, foil, not light tested, 100x100mm, thickness 0.006mm, temporary acrylic support, 99.8%

社交媒体

LinkedIn icon
Twitter icon
Facebook Icon
Instagram Icon

Merck

科研、开发、生产。

作为生命科学行业的全球领先供应商,我们致力于为科研、生物技术开发和生产,以及制药药物疗法开发和生产提供各类解决方案和服务。

© 2021年版权归德国达姆施塔特默克集团(Merck KGaA)及/或其附属公司所有。版权所有。

未经许可,严禁复制本网站上的任何资料。