  • Evaluation of zeolite-sand mixtures as reactive materials protecting groundwater at waste disposal sites.

Evaluation of zeolite-sand mixtures as reactive materials protecting groundwater at waste disposal sites.

Journal of environmental sciences (China) (2014-02-14)
Fronczyk Joanna, Garbulewski Kazimierz
ABSTRACT

To recognize properties of a mixture of Vistula sand (medium sand acc. to USCS) with Slovak zeolite as reactive materials suitable for permeable reactive barriers proposed for protection of groundwater environment in vicinity of old landfills comprehensive laboratory investigations were performed. The present study investigates the removal of contaminants specific for landfill leachates onto zeolite-sand mixtures containing 20%, 50% and 80% of zeolite (ZS20, ZS50 and ZS80). Taking into account the results of batch tests it was concluded that the Langmuir isotherm best fitted the data. It was observed that the presence of ammonium, calcium and magnesium decreases the removal efficiency of copper by 32%. Column tests of contaminant migration through the attenuation zone of the reactive materials were interpreted using the software package CXTFIT, which solves a one-dimensional advection-dispersion equation. Column test results also indicate the strong influence of the presence of interfering substances on copper immobilisation; dynamic sorption capacities decrees twofold. Throughout the landfill leachate flow through ZS80 sample, a constant reduction of NH4+ (at 100%), K+ (at 93%) and Fe(total) (at an average of 86%) were observed. There was no reduction in chemical oxygen demand and biochemical oxygen demand.

MATERIALS
Product Number
Brand
Product Description

Sigma-Aldrich
二氧化硅, nanopowder, 10-20 nm particle size (BET), 99.5% trace metals basis
Sigma-Aldrich
沸石
Sigma-Aldrich
LUDOX® HS-40胶态氧化硅, 40 wt. % suspension in H2O
Sigma-Aldrich
二氧化硅, nanoparticles, mesoporous, 200 nm particle size, pore size 4 nm
Sigma-Aldrich
LUDOX ® AS-40 胶态二氧化硅, 40 wt. % suspension in H2O
Sigma-Aldrich
LUDOX® TM-50 胶态氧化硅, 50 wt. % suspension in H2O
Sigma-Aldrich
二氧化硅, nanopowder (spherical, porous), 5-20 nm particle size (TEM), 99.5% trace metals basis
Sigma-Aldrich
二氧化硅, nanopowder, spec. surface area 175-225 m2/g (BET), 99.8% trace metals basis
Sigma-Aldrich
介孔结构的二氧化硅, MCM-41 type (hexagonal)
Sigma-Aldrich
LUDOX ® AS-30 胶态二氧化硅, 30 wt. % suspension in H2O
Sigma-Aldrich
LUDOX®SM胶体二氧化硅, 30 wt. % suspension in H2O
Sigma-Aldrich
LUDOX ® AM 胶态二氧化硅, 30 wt. % suspension in H2O
Sigma-Aldrich
LUDOX ® TMA 胶态二氧化硅, 34 wt. % suspension in H2O
Sigma-Aldrich
LUDOX ® HS-30 胶态二氧化硅, 30 wt. % suspension in H2O
Sigma-Aldrich
介孔结构的硅铝酸盐, MCM-41 (hexagonal)
Sigma-Aldrich
LUDOX ® TM-40 胶态二氧化硅, 40 wt. % suspension in H2O
Sigma-Aldrich
LUDOX® CL 胶态氧化硅, 30 wt. % suspension in H2O
Sigma-Aldrich
二氧化硅
Sigma-Aldrich
LUDOX® LS 胶态氧化硅, 30 wt. % suspension in H2O
Sigma-Aldrich
LUDOX® CL-X 胶态氧化硅, 45 wt. % suspension in H2O
Sigma-Aldrich
介孔结构的二氧化硅, MSU-F (cellular foam)
Sigma-Aldrich
二氧化硅,氧化铝掺杂型, nanoparticles, dispersion, <50 nm particle size, 20 wt. % in H2O, 99.99% trace metals basis
Sigma-Aldrich
二氧化硅, MSU-H (large pore 2D hexagonal)
Sigma-Aldrich
介孔结构的二氧化硅, HMS (wormhole)