Elastic characterization of nanoporous gold foams using laser based ultrasonics.

Ultrasonics (2014-02-14)
Phillip Ahn, Oluwaseyi Balogun
摘要

A resonance based laser ultrasonics technique is explored for the characterization of low density nanoporous gold foams. Laser generated zero group velocity (ZGV) lamb waves are measured in the foams using a Michelson interferometer. The amplitude spectra obtained from the processed time-domain data are analyzed using a theoretical model from which the foam Young's modulus and Poisson's ratio are obtained. The technique is non-contact and nondestructive, and the ZGV resonance modes are spatially localized, allowing for spatial mapping of the bulk sample properties. The technique may be suitable for process control monitoring and mechanical characterization of low density nanoporous structures.

材料
货号
品牌
产品描述

Sigma-Aldrich
金, foil, thickness 0.127 mm, 99.99% trace metals basis
Sigma-Aldrich
金, nanopowder, <100 nm particle size, 99.9% trace metals basis
Sigma-Aldrich
金, wire, diam. 0.25 mm, ≥99.9% trace metals basis
Sigma-Aldrich
镀金显微镜载片, layer thickness 100 Å, 99.999% (Au)
Sigma-Aldrich
金, foil, thickness 0.5 mm, 99.99% trace metals basis
Sigma-Aldrich
金, powder, <45 μm, 99.99% trace metals basis
Sigma-Aldrich
金, beads, 1-6 mm, 99.999% trace metals basis
Sigma-Aldrich
金, foil, thickness 0.1 mm, 99.99% trace metals basis
Sigma-Aldrich
金, foil, thickness 0.025 mm, 99.99% trace metals basis
Sigma-Aldrich
金, wire, diam. 0.5 mm, 99.99% trace metals basis
Sigma-Aldrich
金, foil, thickness 0.05 mm, 99.99% trace metals basis
Sigma-Aldrich
金, wire, diam. 0.1 mm, 99.99% trace metals basis
Sigma-Aldrich
金, powder, <10 μm, ≥99.9% trace metals basis
Sigma-Aldrich
镀金显微镜载片, layer thickness 1000 Å, 99.999% (Au)
Sigma-Aldrich
金, powder, <850 μm, ≥99.99% trace metals basis
Sigma-Aldrich
金, wire, diam. 0.5 mm, 99.999% trace metals basis
Sigma-Aldrich
金, wire, diam. 1.0 mm, 99.99% trace metals basis
Sigma-Aldrich
金, evaporation slug, diam. × L 0.3 cm × 0.6 cm, 99.99% trace metals basis
Sigma-Aldrich
金, evaporation slug, diam. × L 0.6 cm × 1.2 cm, 99.99% trace metals basis
Sigma-Aldrich
金, wire, diam. 0.25 mm, 99.99% trace metals basis
Sigma-Aldrich
金, foil, thickness 0.25 mm, ≥99.9% trace metals basis
Sigma-Aldrich
金, wire, diam. 0.127 mm, 99.99% trace metals basis
Sigma-Aldrich
镀金盖玻片, 99.999% (Au), diam. × thickness 15 mm × 130-170 μm, layer thickness 100 Å
Sigma-Aldrich
镀金盖玻片, 99.999% (Au), layer thickness 100 Å, L × W × thickness 22 mm × 22 mm × 130-170 μm, square
Sigma-Aldrich
金, wire, diam. 1.0 mm, 99.997% trace metals basis
Sigma-Aldrich
金, wire, diam. 2.0 mm, 99.99% trace metals basis
Sigma-Aldrich
金, rod, diam. 3.0 mm, 99.99% trace metals basis
Sigma-Aldrich
金, wire, diam. 1.5 mm, 99.999% trace metals basis