  • Ordered hexagonal mesoporous aluminosilicates with low Si/Al ratio: synthesis, characterization, and catalytic application.

Ordered hexagonal mesoporous aluminosilicates with low Si/Al ratio: synthesis, characterization, and catalytic application.

Journal of nanoscience and nanotechnology (2014-04-18)
Aifeng Liu, Hongwei Che, Chuanzhi Liu, Quanrong Fu, Ruijiao Jiang, Cheng Wang, Liang Wang
摘要

Ordered hexagonal mesoporous aluminosilicates with lower Si/Al ratio below 5 have been successfully synthesized via the co-assembly of preformed aluminosilicate precursors with Gemini surfactant [C12H25N+(CH3)2(CH2)6N+(CH3)2C12H25] x 2Br(-) as the template. Powder X-ray diffraction, transmission electron microscopy, scanning electron microscopy, N2 adsorption-desorption isotherm measurements, Fourier transform infrared spectroscopy, 27Al nuclear magnetic resonance, thermogravimetric analysis, and temperature-programmed desorption of cyclohexylamine are employed to characterize the resulting samples. The phenol alkylation reaction is carried out to evaluate their catalytic performances. These studies indicate that the sample with a low Si/Al ratio of 3 still retains a highly ordered hexagonal mesoporous structure. And it also possesses the highest acidity of 0.96 mmol among the samples with lower Si/Al ratios below 5 due to its higher specific surface area together with more content of tetrahedrally coordinated Al in the framework. The catalytic tests confirm that the acidity of the samples plays a key role in determining their catalytic performances.

材料
货号
品牌
产品描述

Sigma-Aldrich
环己胺, ReagentPlus®, ≥99.9%
Sigma-Aldrich
硅, powder, −325 mesh, 99% trace metals basis
Sigma-Aldrich
硅, nanopowder, <100 nm particle size (TEM), ≥98% trace metals basis
Sigma-Aldrich
红柱石
Sigma-Aldrich
铝, foil, thickness 0.45-0.55 mm, 99.999% trace metals basis
Sigma-Aldrich
铝, granular, <1 mm, 99.7% trace metals basis
Sigma-Aldrich
硅, wafer (single side polished), <100>, N-type, contains no dopant, diam. × thickness 2 in. × 0.5 mm
Sigma-Aldrich
硅, wafer (single side polished), <100>, P-type, contains boron as dopant, diam. × thickness 3 in. × 0.5 mm
Sigma-Aldrich
硅, wafer (single side polished), <111>, N-type, contains no dopant, diam. × thickness 2 in. × 0.5 mm
Sigma-Aldrich
铝, wire, diam. 1.0 mm, 99.999% trace metals basis
Sigma-Aldrich
铝, ReagentPlus®, beads, 5-15 mm, 99.9% trace metals basis
Sigma-Aldrich
铝, foil, thickness 0.25 mm, 99.999% trace metals basis
Sigma-Aldrich
铝, pellets, 3-12 mm, 99.99% trace metals basis
Sigma-Aldrich
铝, evaporation slug, diam. × L 6.3 mm × 6.3 mm, 99.999% trace metals basis
Sigma-Aldrich
硅, wafer (single side polished), <100>, P-type, contains boron as dopant, diam. × thickness 2 in. × 0.5 mm
Sigma-Aldrich
硅, pieces, 99.95% trace metals basis
Sigma-Aldrich
铝, wire, diam. 0.58 mm, ≥99.99% trace metals basis
Sigma-Aldrich
铝, ≤30 μm, spherical powder, ≥99%
Sigma-Aldrich
硅, powder, −60 mesh, 99.998% trace metals basis
Sigma-Aldrich
铝, foil, thickness 0.13 mm, ≥99.99% trace metals basis
Sigma-Aldrich
硅, wafer (single side polished), <100>, N-type, contains phosphorus as dopant, diam. × thickness 2 in. × 0.5 mm
Sigma-Aldrich
铝, pellets, 3-8 mesh, ≥99.999% trace metals basis
Sigma-Aldrich
硅, wafer (single side polished), <100>, N-type, contains no dopant, diam. × thickness 3 in. × 0.5 mm
Sigma-Aldrich
铝, ACS reagent, 99%, wire, wire diam. ~1.5 mm
Sigma-Aldrich
铝, rod, diam. × L 3.0 mm × 100 mm, 99.999% trace metals basis
硅, rod, 40mm, diameter 20mm, single crystal, -100, 99.999%
铝, IRMM®, certified reference material, 0.1 mm foil
铝, wire reel, 25m, diameter 0.25mm, as drawn, 99.5%
硅, rod, 100mm, diameter 10.0mm, single crystal - random orientation, 100%
硅, disks, 15.9mm, thickness 0.38mm, single crystal, n-type, 100%