  • Direct evidence of spatially selective iron mineralization using an immobilized ferritin protein cage.

Direct evidence of spatially selective iron mineralization using an immobilized ferritin protein cage.

Journal of nanoscience and nanotechnology (2014-04-17)
Koichiro Uto, Kazuya Yamamoto, Naoko Kishimoto, Masahiro Muraoka, Takao Aoyagi, Ichiro Yamashita
ABSTRACT

(Apo)ferritins are cage-shaped proteins which have recently received a great deal of attention because the inner cavity of the protein shell can be used as a size-restricted reaction field for the synthesis of nanomaterials. The biomineralization behavior and inorganic nanoparticle (NP) synthesis mechanism of (apo)ferritin in solution systems have been studied but the mineralization behavior of (apo)ferritin on the substrates has not yet been well studied. Here, we conducted quantitative and kinetic analyses of the mineralization behavior of immobilized (apo)ferritin on a polyelectrolyte multilayer (PEM) using quartz crystal microbalance (QCM), scanning electron microscopy (SEM), and X-ray photoelectron spectroscopy (XPS) techniques. We demonstrated that the (apo)ferritin immobilized on a substrate synthesizes a ferrihydrite core within the confines of the protein cage; similar to a solution dispersed system. In addition, we applied a ferritin/apoferritin blended monolayer to the study of iron mineralization and revealed that biomineralization in this system is spatially selective. It is important to understand the mineralization mechanisms for the synthesis of other functional NPs as this approach has potential for a broad range of magnetic, catalytic, and biomedical sensing applications.

MATERIALS
Product Number
Brand
Product Description

Sigma-Aldrich
氧化铁(III), powder, <5 μm, ≥96%
Sigma-Aldrich
铁, ≥99%, reduced, powder (fine)
Sigma-Aldrich
氧化铁(III), nanopowder, <50 nm particle size (BET)
Sigma-Aldrich
铁蛋白 来源于马脾脏, Type I, saline solution
Sigma-Aldrich
羰基铁, ≥97% Fe basis
Sigma-Aldrich
氧化铁(III), ≥99.995% trace metals basis
Sigma-Aldrich
铁, puriss. p.a., carbonyl-Iron powder, low in magnesium and manganese compounds, ≥99.5% (RT)
Sigma-Aldrich
铁, granular, 10-40 mesh, >99.99% trace metals basis
Sigma-Aldrich
铁, foil, thickness 0.1 mm, ≥99.9% trace metals basis
Sigma-Aldrich
铁蛋白 来源于人类肝脏, Type IV, 10 μg/mL
Sigma-Aldrich
铁, chips, 99.98% trace metals basis
Sigma-Aldrich
氧化亚铁(II),分散体, nanoparticles, ≤110 nm particle size, 15 wt. % in ethanol
Sigma-Aldrich
铁, foil, thickness 0.25 mm, ≥99.99% trace metals basis
Sigma-Aldrich
铁, wire, diam. 1.0 mm, ≥99.9% trace metals basis
Sigma-Aldrich
铁蛋白 来源于人类脾脏, Type V, 10 μg/mL in 0.15 M NaCl, 10 mM Tris, pH 8.0, containing 0.1% sodium azide
Sigma-Aldrich
铁, carbon coated magnetic, nanopowder, 25 nm avg. part. size, 99.5% trace metals basis
Sigma-Aldrich
铁, wire, diam. 0.5 mm, ≥99.9% trace metals basis
铁, foil, 300x300mm, thickness 0.1mm, hard, 99.5%
Sigma-Aldrich
铁, wire, diam. 1.0 mm, ≥99.99% trace metals basis
铁, rod, 200mm, diameter 2.0mm, as drawn, 99.99+%
铁, rod, 50mm, diameter 5.0mm, as drawn, 99.99+%
铁, wire reel, 5m, diameter 0.025mm, as drawn, 99.99+%
铁, foil, 100x100mm, thickness 0.25mm, hard, 99.5%
铁, foil, 300x300mm, thickness 0.38mm, hard, 99.5%
铁, foil, 100x100mm, thickness 1.5mm, as rolled, 99.5%
铁, foil, 10mm disks, thickness 0.01mm, 99.85%
铁, foil, 10mm disks, thickness 0.01mm, 99.99+%
铁, foil, 10mm disks, thickness 0.020mm, 99.85%
铁, foil, 10mm disks, thickness 0.025mm, as rolled, 99.99+%
铁, foil, 10mm disks, thickness 0.025mm, hard, 99.5%