Preparation of cocrystal nanofibres of cobalt octaethylporphyrin and tetracyanoquinodimethane with good photoresponse.

Journal of nanoscience and nanotechnology (2014-04-18)
Hao-Di Wu, Yan Xiao, Feng-Xia Wang, Ge-Bo Pan
摘要

Cocrystal nanofibres of cobalt octaethylporphyrin and tetracyanoquinodimethane were prepared by a facile solution method and fully characterized by SEM, AFM, XRD, Raman, EDX, and UV-vis-NIR. The as-prepared cocrystal nanofibres had smooth surfaces and uniform dimension. When incorporated into prototype devices, they exhibited good photoresponse at ambient conditions. Additionally, the phototransistor characteristics with a maximum I(on)/I(off) ratio of -460 was demonstrated. The facile synthesis and good photoresponse may boost the potential applications of cocrystal-based nanostructures in future miniaturized devices.

材料
货号
品牌
产品描述

Sigma-Aldrich
钴, powder, <150 μm, ≥99.9% trace metals basis
Sigma-Aldrich
钴, powder, 2 μm particle size, 99.8% trace metals basis
Sigma-Aldrich
钴, Carbon coated magnetic, nanopowder, <50 nm particle size (TEM), ≥99%
Sigma-Aldrich
钴, granular, 99.99% trace metals basis
Sigma-Aldrich
钴, foil, thickness 0.1 mm, 99.95% trace metals basis
Sigma-Aldrich
钴, pieces, 99.5% trace metals basis
Sigma-Aldrich
钴, wire, diam. 1.0 mm, 99.995% trace metals basis
Sigma-Aldrich
钴, foil, thickness 0.25 mm, ≥99.99% trace metals basis
钴, foil, 25x25mm, thickness 0.25mm, as rolled, 99.99+%
钴, foil, 100x100mm, thickness 0.125mm, annealed, 99.9%
钴, wire reel, 0.2m, diameter 0.125mm, hard, 99.99+%
钴, foil, 25mm disks, thickness 0.05mm, annealed, 99.9%
钴, foil, 25mm disks, thickness 0.05mm, as rolled, 99.9%
钴, foil, 25mm disks, thickness 0.125mm, annealed, 99.9%
钴, foil, 25mm disks, thickness 0.25mm, as rolled, 99.9%
钴, foil, 25mm disks, thickness 0.25mm, as rolled, 99.99+%
钴, foil, 4mm disks, thickness 0.003mm, 99.9%
钴, foil, 4mm disks, thickness 0.004mm, 99.9%
钴, foil, 4mm disks, thickness 0.005mm, 99.9%
钴, foil, 4mm disks, thickness 0.006mm, 99.9%
钴, foil, 4mm disks, thickness 0.007mm, 99.9%
钴, foil, 4mm disks, thickness 0.008mm, 99.9%
钴, foil, 4mm disks, thickness 0.009mm, 99.9%
钴, foil, 4mm disks, thickness 0.0125mm, 99.9%
钴, foil, 4mm disks, thickness 0.015mm, 99.9%
钴, foil, 4mm disks, thickness 0.01mm, 99.9%
钴, foil, 4mm disks, thickness 0.025mm, 99.9%
钴, foil, 4mm disks, thickness 0.02mm, 99.9%
钴, foil, 4mm disks, thickness 0.05mm, annealed, 99.9%
钴, foil, 4mm disks, thickness 0.05mm, as rolled, 99.9%