  • Hybrid macroporous gelatin/bioactive-glass/nanosilver scaffolds with controlled degradation behavior and antimicrobial activity for bone tissue engineering.

Hybrid macroporous gelatin/bioactive-glass/nanosilver scaffolds with controlled degradation behavior and antimicrobial activity for bone tissue engineering.

Journal of biomedical nanotechnology (2014-04-23)
M Yazdimamaghani, D Vashaee, S Assefa, K J Walker, S V Madihally, G A Köhler, L Tayebi
摘要

A new composition of gelatin/bioactive-glass/silver nanoparticle was synthesized and employed to prepare antibacterial macroporous scaffolds with potential applications in bone tissue engineering. A set of macroporous nanocomposite scaffolds were developed from an aqueous solution of gelatin by freeze-drying and crosslinking using genipin at ambient temperature. Silver nanoparticles were successfully synthesized in situ in gelatin solution by heat treatment reduction as a simple and "green" method in which gelatin acted as a natural reducing and stabilizing agent. The effect of the incorporation of the bioactive-glass and the silver nanoparticle concentration on the physicochemical properties of the scaffolds, such as the gel fraction, porosity, in vitro enzyme degradation, morphology, and swelling behavior was studied. Furthermore, the in vitro viability of human mesenchymal stem cells (hMSC) and the antibacterial activity against gram-negative Escherichia coli and gram-positive Staphylococcus aureus were tested on the scaffolds. It was found that upon the addition of silver nanoparticles the porosity, pore size, swelling, and antibacterial properties were enhanced. The silver nanoparticles increased the in vitro enzyme degradation in samples without bioactive-glass; however, the degradation was remarkably reduced by addition of bioactive-glass. In addition, formation of apatite particles, the main inorganic constituent of the bone, on the surface of the bioactive-glass containing scaffolds were confirmed after immersion in simulated body fluid (SBF). The viability of hMSC on the scaffold suggested that gelatin/bioactive-glass/nanosilver scaffolds can be used as an antibacterial scaffolds.

材料
货号
品牌
产品描述

Sigma-Aldrich
明胶 溶液, Type B, 2% in H2O, tissue culture grade, BioReagent, suitable for cell culture
Sigma-Aldrich
明胶 来源于猪皮肤, powder, gel strength ~300 g Bloom, Type A, BioReagent, suitable for electrophoresis, suitable for cell culture
Sigma-Aldrich
明胶 来源于猪皮肤, gel strength 300, Type A
Sigma-Aldrich
明胶 来源于冷水鱼类的皮肤, solid
Sigma-Aldrich
明胶 来源于牛皮, Type B, powder, BioReagent, suitable for cell culture
Sigma-Aldrich
银, conductive paste
Sigma-Aldrich
明胶 来源于牛皮, gel strength ~225 g Bloom, Type B
Sigma-Aldrich
明胶, tested according to Ph. Eur.
Sigma-Aldrich
明胶 来源于牛皮, Type B
Sigma-Aldrich
明胶 来源于猪皮肤, gel strength ~175 g Bloom, Type A
Sigma-Aldrich
明胶 来源于猪皮肤, gel strength 80-120 g Bloom, Type A
Millipore
明胶 来源于猪皮肤, medium gel strength, suitable for microbiology
Sigma-Aldrich
明胶 来源于猪皮肤, Type A, lyophilized powder, γ-irradiated, BioXtra, suitable for cell culture
Sigma-Aldrich
Prionex® Highly purified Type A, aqueous solution
Millipore
明胶 来源于猪皮肤, powder, suitable for microbiology
Sigma-Aldrich
银, foil, thickness 1.0 mm, 99.99% trace metals basis
Millipore
明胶 来源于猪皮肤, suitable for microbiology, high gel strength
Millipore
明胶 来源于猪皮肤, suitable for microbiology, low gel strength
Millipore
明胶 来源于猪皮肤, suitable for microbiology, ultrahigh gel strength
银, rod, 1000mm, diameter 3.0mm, as drawn, 99.997%
银, wire reel, 50m, diameter 0.05mm, annealed, 99.99%
银, foil, light tested, 50x50mm, thickness 0.05mm, annealed, 99.95+%
银, foil, 100x100mm, thickness 0.5mm, as rolled, 99.99+%
银, insulated wire, 10m, conductor diameter 0.05mm, insulation thickness 0.0075mm, polyester insulation, 99.99%
银, wire reel, 50m, diameter 0.25mm, annealed, 99.99%
银, foil, 10mm disks, thickness 1.0mm, as rolled, 99.95+%
银, wire reel, 5m, diameter 0.5mm, annealed, 99.99%
银, foil, 25x25mm, thickness 1.0mm, as rolled, 99.95+%
银, wire reel, 5m, diameter 0.25mm, annealed, 99.99%
银, rod, 100mm, diameter 1.5mm, as drawn, 99.95+%