Sorptive extraction using polydimethylsiloxane/metal-organic framework coated stir bars coupled with high performance liquid chromatography-fluorescence detection for the determination of polycyclic aromatic hydrocarbons in environmental water samples.

Journal of chromatography. A (2014-07-09)
Cong Hu, Man He, Beibei Chen, Cheng Zhong, Bin Hu
摘要

In this work, metal-organic frameworks (MOFs, Al-MIL-53-NH₂) were synthesized via the hydrothermal method, and novel polydimethylsiloxane/metal-organic framework (PDMS/MOFs, PDMS/Al-MIL-53-NH₂)-coated stir bars were prepared by the sol-gel technique. The preparation reproducibility of the PDMS/MOFs-coated stir bar was good, with relative standard deviations (RSDs) ranging from 4.8% to 14.9% (n=7) within one batch and from 6.2% to 16.9% (n=6) among different batches. Based on this fact, a new method of PDMS/MOFs-coated stir bar sorptive extraction (SBSE) and ultrasonic-assisted liquid desorption (UALD) coupled with high performance liquid chromatography-fluorescence detection (HPLC-FLD) was developed for the determination of polycyclic aromatic hydrocarbons (PAHs) in environmental water samples. To obtain the best extraction performance for PAHs, several parameters affecting SBSE, such as extraction time, stirring rate, and extraction temperature, were investigated. Under optimal experimental conditions, wide linear ranges and good RSDs (n=7) were obtained. With enrichment factors (EFs) of 16.1- to 88.9-fold (theoretical EF, 142-fold), the limits of detection (LODs, S/N=3) of the developed method for the target PAHs were found to be in the range of 0.05-2.94 ng/L. The developed method was successfully applied to the analysis of PAHs in Yangtze River and East Lake water samples.

材料
货号
品牌
产品描述

Sigma-Aldrich
硅油, for oil baths (from −50°C to +200°C)
Sigma-Aldrich
硅油, viscosity 5 cSt (25 °C)
Sigma-Aldrich
硅油, viscosity 10 cSt (25 °C)
Sigma-Aldrich
硅油, viscosity 20 cSt (25 °C)
Sigma-Aldrich
硅油, Dow Corning 200® fluid, viscosity 60,000 cSt (25 °C)
Sigma-Aldrich
硅油, viscosity 100 cSt (25 °C)
Sigma-Aldrich
硅油, viscosity 1,000 cSt (25 °C)
Sigma-Aldrich
硅油, viscosity 350 cSt (25 °C)
Sigma-Aldrich
硅油, viscosity 10,000 cSt (25 °C)
硅油, for melting point and boiling point apparatuses
Sigma-Aldrich
硅油, viscosity 50 cSt (25 °C)
Sigma-Aldrich
铝, foil, thickness 0.45-0.55 mm, 99.999% trace metals basis
Sigma-Aldrich
铝, foil, thickness 0.25 mm, 99.999% trace metals basis
Sigma-Aldrich
硅油, viscosity 500 cSt (25 °C)
Sigma-Aldrich
铝, wire, diam. 1.0 mm, 99.999% trace metals basis
Sigma-Aldrich
铝, wire, diam. 0.58 mm, ≥99.99% trace metals basis
Sigma-Aldrich
硅油, viscosity 30,000 cSt (25 °C)
Sigma-Aldrich
硅油, viscosity 100,000 cSt (25 °C)
硅油, European Pharmacopoeia (EP) Reference Standard
Sigma-Aldrich
铝, granular, <1 mm, 99.7% trace metals basis
Sigma-Aldrich
铝, ReagentPlus®, beads, 5-15 mm, 99.9% trace metals basis
Sigma-Aldrich
铝, evaporation slug, diam. × L 6.3 mm × 6.3 mm, 99.999% trace metals basis
Sigma-Aldrich
铝, ≤30 μm, spherical powder, ≥99%
Sigma-Aldrich
铝, pellets, 3-12 mm, 99.99% trace metals basis
铝, rod, 100mm, diameter 12.7mm, 99%
Sigma-Aldrich
铝, foil, thickness 0.13 mm, ≥99.99% trace metals basis
Sigma-Aldrich
铝, foil, thickness 1.0 mm, 99.999% trace metals basis
Sigma-Aldrich
铝, ACS reagent, 99%, wire, wire diam. ~1.5 mm
铝, rod, 500mm, diameter 12.7mm, 99%
铝, rod, 100mm, diameter 6.0mm, as drawn, 99.999%