  • Fast and continuous preparation of high polymerization degree cellulose nanofibrils and their three-dimensional macroporous scaffold fabrication.

Fast and continuous preparation of high polymerization degree cellulose nanofibrils and their three-dimensional macroporous scaffold fabrication.

Nanoscale (2013-02-16)
Jiankang Song, Aimin Tang, Tingting Liu, Jufang Wang
ABSTRACT

C6-carboxy-cellulose with a carboxylate content of 0.8 mmol g(-1) was obtained by oxidation of once-dried cellulose, using the 2,2,6,6-tetramethylpiperidinyl-1-oxyl (TEMPO)/NaClO/NaClO2 system at pH 6.8 and 60 °C for 16 h. This method, with the addition of reagents in the order TEMPO, NaClO and NaClO2, was 38 h faster than a previously published method. Individualized cellulose nanofibrils with a width of 3-5 nm and a length of several hundred nanometers were prepared by homogenizing the C6-carboxy-cellulose-water suspension. Macroporous cellulose nanofibril/poly(vinyl alcohol) scaffolds with interconnected large pores of 20-100 μm diameter and small pores of 2-10 μm diameter were fabricated. The cellulose nanofilaments formed nanofibrous structures on the surface of the PVA wall, which was similar to that of the collagen skeleton of the extracellular matrix. NIH/3T3 cells were cultured in the scaffolds for 4 weeks, SEM observation showed that the cells were anchored and clustered on the cellulose nanofilaments, forming spherical colonies. The extracellular matrix (ECM) was filled with mineralized particles.

MATERIALS
Product Number
Brand
Product Description

Sigma-Aldrich
Perchloric acid, ACS reagent, 70%
Sigma-Aldrich
Poly(vinyl alcohol), Mw 89,000-98,000, 99+% hydrolyzed
Sigma-Aldrich
Sodium perchlorate, ACS reagent, ≥98.0%
Sigma-Aldrich
TEMPO, 98%
Sigma-Aldrich
Poly(vinyl alcohol), Mw 9,000-10,000, 80% hydrolyzed
Sigma-Aldrich
Poly(vinyl alcohol), 87-90% hydrolyzed, average mol wt 30,000-70,000
Sigma-Aldrich
Mowiol® 4-88, Mw ~31,000
Sigma-Aldrich
Perchloric acid, 70%, 99.999% trace metals basis
Sigma-Aldrich
Poly(vinyl alcohol), Mw 13,000-23,000, 87-89% hydrolyzed
Sigma-Aldrich
Poly(vinyl alcohol), Mw 146,000-186,000, 99+% hydrolyzed
Sigma-Aldrich
Poly(vinyl alcohol), Mw 85,000-124,000, 99+% hydrolyzed
Sigma-Aldrich
Perchloric acid, ACS reagent, 60%
Sigma-Aldrich
Poly(vinyl alcohol), Mw 31,000-50,000, 98-99% hydrolyzed
Sigma-Aldrich
Poly(vinyl alcohol), average Mw 13,000-23,000, 98% hydrolyzed
Sigma-Aldrich
Sodium chlorate, ACS reagent, ≥99.0%
Sigma-Aldrich
Poly(vinyl alcohol), average Mw 85,000-124,000, 87-89% hydrolyzed
Sigma-Aldrich
Perchloric acid, puriss. p.a., ACS reagent, reag. ISO, reag. Ph. Eur., 70.0-72.0%
Sigma-Aldrich
Poly(vinyl alcohol), Fully hydrolyzed
Sigma-Aldrich
Poly(vinyl alcohol), average Mw 31,000-50,000, 87-89% hydrolyzed
Sigma-Aldrich
TEMPO, purified by sublimation, 99%
Sigma-Aldrich
Mowiol® 10-98, Mw ~61,000
Sigma-Aldrich
Mowiol® 18-88, Mw ~130,000
Sigma-Aldrich
Poly(vinyl alcohol), average Mw 146,000-186,000, 87-89% hydrolyzed
Sigma-Aldrich
Poly(vinyl alcohol), average Mw 130,000, 99+% hydrolyzed
Sigma-Aldrich
Mowiol® 40-88, average Mw ~205,000 g/mol
Sigma-Aldrich
Mowiol® 4-98, Mw ~27,000
Sigma-Aldrich
Mowiol® 8-88, Mw ~67,000
Sigma-Aldrich
Mowiol® 28-99, Mw ~145,000
Sigma-Aldrich
Mowiol® 20-98, Mw ~125,000
Supelco
Perchloric acid concentrate, 0.01 M HClO4 in water (0.01N), eluent concentrate for IC