  • An investigation on the influence of tin foil substitute contamination on bond strength between resin denture teeth and the denture base: an in vitro study.

An investigation on the influence of tin foil substitute contamination on bond strength between resin denture teeth and the denture base: an in vitro study.

Indian journal of dental research : official publication of Indian Society for Dental Research (2012-12-22)
Sapna Bhaskaran, R B Hallikerimath
摘要

The problem of acrylic resin denture teeth separating from their denture base remains a major problem in prosthodontic practice and is frustrating to the patients as well as the dentists. This study investigated the influence of tin foil substitute contamination on bond strength between acrylic resin denture teeth and their denture base. A total of 80 modified acrylic resin maxillary left central incisors were processed to their denture base material. The 80 specimens were divided into two groups of 40 specimens each: the experimental group and the control group. The experimental group had the denture tooth ridge lap area contaminated with tin foil substitute.The 40 specimens in the control group were not contaminated. After 7 days of storage at room temperature, the bond strengths of the two groups were tested with a universal testing machine.The nature of failure was noted as adhesive (interface) or cohesive (in tooth or denture base material). The Welch test and z-test were performed to identify significant differences. The uncontaminated specimens (group I) showed superior bond strength as compared to the contaminated specimens (group II); the difference in bond strength between the groups was highly significant (P<0.0001). Also the contaminated specimens exhibited predominantly adhesive failure (89.74%), whereas the uncontaminated specimens exhibited 55% adhesive failure and 45% cohesive failure. Tin foil substitute contamination of the ridge laps of acrylic resin denture teeth greatly reduced the bond strength.

材料
货号
品牌
产品描述

锡, foil, 150x150mm, thickness 0.20mm, as rolled, 98.8%
锡, foil, 0.5m coil, thickness 0.009mm, 97.4%
锡, foil, 100x100mm, thickness 0.125mm, as rolled, 98.8%
锡, foil, 100x100mm, thickness 0.125mm, as rolled, 99.99+%
锡, foil, 100x100mm, thickness 0.15mm, as rolled, 98.8%
锡, foil, 100x100mm, thickness 0.15mm, as rolled, 99.99+%
锡, foil, 100x100mm, thickness 0.1mm, as rolled, 98.8%
锡, foil, 100x100mm, thickness 0.1mm, as rolled, 99.95%
锡, foil, 100x100mm, thickness 0.20mm, as rolled, 98.8%
锡, foil, 100x100mm, thickness 0.25mm, as rolled, 98.8%
锡, foil, 100x100mm, thickness 0.25mm, as rolled, 99.99+%
锡, foil, 100x100mm, thickness 0.5mm, as rolled, 98.8%
锡, foil, 100x100mm, thickness 0.5mm, as rolled, 99.99+%
锡, foil, 100x100mm, thickness 0.65mm, as rolled, 99.99+%
锡, foil, 100x100mm, thickness 0.75mm, as rolled, 99.99+%
锡, foil, 100x100mm, thickness 1.0mm, as rolled, 98.8%
锡, foil, 100x100mm, thickness 1.0mm, as rolled, 99.99+%
锡, foil, 100x100mm, thickness 1.0mm, as rolled, 99.999%
锡, foil, 100x100mm, thickness 1.5mm, as rolled, 99.99+%
锡, foil, 100x100mm, thickness 2.0mm, as rolled, 98.8%
锡, foil, 100x100mm, thickness 2.0mm, as rolled, 99.99+%
锡, foil, 150x150mm, thickness 0.125mm, as rolled, 98.8%
锡, foil, 150x150mm, thickness 0.125mm, as rolled, 99.99+%
锡, foil, 150x150mm, thickness 0.15mm, as rolled, 98.8%
锡, foil, 150x150mm, thickness 0.1mm, as rolled, 98.8%
锡, foil, 150x150mm, thickness 0.1mm, as rolled, 99.95%
锡, foil, 150x150mm, thickness 0.25mm, as rolled, 98.8%
锡, foil, 150x150mm, thickness 0.25mm, as rolled, 99.99+%
锡, foil, 150x150mm, thickness 0.5mm, as rolled, 98.8%
锡, foil, 150x150mm, thickness 0.5mm, as rolled, 99.99+%

社交媒体

LinkedIn icon
Twitter icon
Facebook Icon
Instagram Icon

Merck

科研、开发、生产。

作为生命科学行业的全球领先供应商,我们致力于为科研、生物技术开发和生产,以及制药药物疗法开发和生产提供各类解决方案和服务。

© 2021年版权归德国达姆施塔特默克集团(Merck KGaA)及/或其附属公司所有。版权所有。

未经许可,严禁复制本网站上的任何资料。