Controlled one-step fabrication of highly oriented ZnO nanoneedle/nanorods arrays at near room temperature.

Chemical communications (Cambridge, England) (2006-04-04)
Xufeng Wu, Hua Bai, Chun Li, Gewu Lu, Gaoquan Shi
RESUMEN

Highly oriented ZnO nanoneedle/nanorods arrays have been fabricated by direct oxidation of zinc foil in alkaline zincate ion solution at near room temperature (20 degrees C for nanoneedles, 30 degrees C for nanorods).

MATERIALES
Referencia del producto
Marca
Descripción del producto

Cinc, foil, 300x300mm, thickness 0.1mm, as rolled, 99.95+%
Cinc, foil, 100x100mm, thickness 0.1mm, as rolled, 99.95+%
Cinc, foil, 150x150mm, thickness 0.1mm, as rolled, 99.95+%
Cinc, foil, 50x50mm, thickness 0.15mm, as rolled, 99.95+%
Cinc, foil, 100x100mm, thickness 6mm, as rolled, 99.99+%
Cinc, foil, 100x100mm, thickness 0.15mm, as rolled, 99.95+%
Cinc, foil, 100x100mm, thickness 0.175mm, as rolled, 99.95+%
Cinc, foil, 300x300mm, thickness 0.35mm, as rolled, 99.95+%
Cinc, foil, 300x300mm, thickness 2.0mm, as rolled, 99.95+%
Cinc, foil, 25x25mm, thickness 6mm, as rolled, 99.99+%
Cinc, foil, light tested, 150x150mm, thickness 0.05mm, as rolled, 99.95+%
Cinc, foil, 1m coil, thickness 0.05mm, as rolled, 99.95+%
Cinc, foil, 150x150mm, thickness 0.15mm, as rolled, 99.95+%
Cinc, foil, 6mm disks, thickness 0.015mm, 99.9%
Cinc, foil, 10mm disks, thickness 0.25mm, as rolled, 99.99+%
Cinc, foil, 8mm disks, thickness 0.01mm, 99.9%
Cinc, foil, 50x50mm, thickness 0.1mm, as rolled, 99.95+%
Cinc, foil, 10mm disks, thickness 0.015mm, 99.9%
Cinc, foil, 1m coil, thickness 0.125mm, as rolled, 99.95+%