Meta-analysis of bonding effectiveness to zirconia ceramics.

Meta-analysis of bonding effectiveness to zirconia ceramics.

Journal of dental research (2014-02-25)

M Inokoshi, J De Munck, S Minakuchi, B Van Meerbeek

ABSTRAKT

Dental zirconia can no longer be considered un-bondable to tooth tissue. In literature, an increasing number of papers indeed report on the bonding effectiveness of different luting techniques to zirconia. We aimed to disclose general trends in bonding to zirconia by systematically collecting zirconia bond-strength data. A search in PubMed and EMBASE revealed 1,371 bond-strength tests reported on in 144 papers. A macro-shear bond-strength protocol was most frequently used; it revealed significantly lower bond strengths and was less discriminative than the other test methods. Regarding luting technique, the combination of mechanical and chemical pre-treatment appeared particularly crucial to obtain durable bonding to zirconia ceramics. The cement choice was not revealed as a determining factor after aging conditions, as long as composite cement was used. Regarding test protocol, a tensile test appeared more discriminative, particularly when combined with 'water storage' aging.

MATERIAŁY

Numer produktu

Marka

Opis produktu

GF06322597

Zirconium, foil, not light tested, 200x300mm, thickness 0.02mm, 99.2%

GF52371941

Zirconium, wire reel, 5m, diameter 0.5mm, as drawn, 99.2%

230693

Sigma-Aldrich

Zirconium(IV) oxide, powder, 5 μm, 99% trace metals basis

544760

Sigma-Aldrich

Zirconium(IV) oxide, nanopowder, <100 nm particle size (TEM)

204994

Sigma-Aldrich

Zirconium(IV) oxide, 99.99% trace metals basis (purity excludes ~2% HfO₂)

267724

Sigma-Aldrich

Zirconium, rod, diam. 6.35 mm, ≥99% trace metals basis

419141

Sigma-Aldrich

Zirconium, foil, thickness 0.1 mm, 99.98% trace metals basis

643025

Sigma-Aldrich

Zirconium(IV) oxide, nanoparticles, dispersion, <100 nm particle size (BET), 10 wt. % in H₂O

GF97239044

Zirconium, tube, 500mm, outside diameter 2.0mm, inside diameter 1.6mm, wall thickness 0.2mm, annealed, 99.2%

GF88851730

Zirconium, tube, 100mm, outside diameter 12.7mm, inside diameter 9.5mm, wall thickness 1.6mm, annealed, 99.2%

GF41005538

Zirconium, rod, 200mm, diameter 9.5mm, centerless ground, 99.2%

GF25691878

Zirconium, rod, 500mm, diameter 9.5mm, centerless ground, 99.2%

GF90246056

Zirconium, rod, 100mm, diameter 3.0mm, centerless ground, 99.2%

GF04678230

Zirconium, tube, 500mm, outside diameter 6.35mm, inside diameter 4.55mm, wall thickness 0.9mm, annealed, 99.2%

GF59501257

Zirconium, sponge, 500g, max. size 25mm, 99.2%

GF84010496

Zirconium, rod, 200mm, diameter 1.5mm, 99.2%

GF48232515

Zirconium, wire reel, 1m, diameter 0.125mm, stress relieved, 99.2%

GF30689040

Zirconium, tube, 200mm, outside diameter 1.6mm, inside diameter 1.1mm, wall thickness 0.25mm, hard, 99.2%

GF40871314

Zirconium, wire reel, 2m, diameter 0.05mm, as drawn, 99.2%

GF70641086

Zirconium, sponge, 50g, max. size 25mm, 99.2%

GF69666610

Zirconium, wire reel, 0.5m, diameter 0.05mm, as drawn, 99.2%

GF44790846

Zirconium, rod, 200mm, diameter 12.7mm, centerless ground, 99.2%

GF92588967

Zirconium, rod, 200mm, diameter 3.0mm, centerless ground, 99.2%

GF66272081

Zirconium, rod, 100mm, diameter 1.5mm, 99.2%

GF53750358

Zirconium, wire reel, 1m, diameter 0.25mm, as drawn, 99.2%

GF49023862

Zirconium, rod, 500mm, diameter 3.0mm, centerless ground, 99.2%

GF04513700

Zirconium, rod, 100mm, diameter 50mm, centerless ground, 99.2%

GF08914664

Zirconium, wire reel, 5m, diameter 0.05mm, as drawn, 99.2%

GF43414556

Zirconium, wire reel, 0.5m, diameter 0.5mm, as drawn, 99.2%

GF35558321

Zirconium, rod, 100mm, diameter 12.7mm, centerless ground, 99.2%