- Water soluble sodium sulfate nanorods as a versatile template for the designing of copper sulfide nanotubes.
Water soluble sodium sulfate nanorods as a versatile template for the designing of copper sulfide nanotubes.
Journal of nanoscience and nanotechnology (2014-04-18)
Gautam Das, Nitul Kakati, Seok Hee Lee, Niranjan Karak, Young Soo Yoon
PMID24738412
ABSTRAKT
The present study reports the use of water soluble sodium sulfate (Na2SO4) nanorods as a versatile template for generation of tubular copper sulfide (CuS) nanostructures. The Na2SO4 nanorods were synthesized from ammonium sulfate (NH4)2SO4 and sodium hydroxide (NaOH), under refluxing condition. The shape and morphology control of the Na2SO4 nanorods were studied with respect to nature of surfactant used and reactant mole ratio. While, PVP mole ratio was important to obtain homogeneous nanorods. Uniform and stable nanotubes of CuS were than obtained by the dissolution of the nanorods in water. The use of simple chemicals for synthesis of such nanotube templates opens the prospect for wide scale downstream applications.
MATERIAŁY
Numer produktu
Marka
Opis produktu
Copper, rod, 500mm, diameter 4.8mm, as drawn, 99.99+%
Copper, insulated wire, 10m, conductor diameter 0.7mm, insulation thickness 0.01mm, polyurethane insulation
Copper, rod, 1000mm, diameter 4.8mm, hard, 99.9%
Copper, mesh, 100x100mm, nominal aperture 0.14mm, thickness 0.25mm, wire diameter 0.115mm, 100x100 wires/inch, open area 30.3%, plain weave mesh
Copper, insulated wire, 20m, conductor diameter 0.5mm, insulation thickness 0.025mm, polyimide insulation, 99.99%
Copper, insulated wire, 20m, conductor diameter 0.05mm, insulation thickness 0.002mm, 2 micron polyesterimide insulation, 99.9%
Copper, rod, 1000mm, diameter 9.5mm, hard, 99.9%
Copper, insulated wire, 20m, conductor diameter 0.24mm, insulation thickness 0.25mm, PTFE (polytetrafluoroethylene) insulation
Copper, rod, 100mm, diameter 2.0mm, as drawn, 99.99+%
Copper, insulated wire, 5m, conductor diameter 0.018mm, insulation thickness 0.005mm, polyurethane insulation, 99.99%
Copper, rod, 200mm, diameter 4.8mm, as drawn, 99.99+%
Copper, rod, 1000mm, diameter 2.0mm, as drawn, 99.99+%
Copper, insulated wire, 5m, conductor diameter 0.4mm, insulation thickness 0.025mm, polyimide insulation, 99.99%
Copper, insulated wire, 20m, conductor diameter 0.7mm, insulation thickness 0.01mm, polyurethane insulation
Copper, rod, 500mm, diameter 6.35mm, as drawn, 99.999%
Copper, rod, 100mm, diameter 9.5mm, as drawn, 99.99+%
Copper, rod, 200mm, diameter 6.35mm, as drawn, 99.999%
Copper, rod, 500mm, diameter 8.0mm, as drawn, 99.99+%
Copper, rod, 1000mm, diameter 4.8mm, as drawn, 99.99+%
Copper, microfoil, disks, 10mm, thinness 0.1μm, specific density 86.2μg/cm2, permanent mylar 3.5μm support, 99.99+%
Copper, rod, 100mm, diameter 5.0mm, as drawn, 99.999%
Copper, insulated wire, 5m, conductor diameter 0.025mm, insulation thickness 0.005mm, polyurethane insulation, 99.99%
Copper, rod, 500mm, diameter 9.5mm, as drawn, 99.99+%
Copper, tube, 1000mm, outside diameter 6.35mm, inside diameter 4.93mm, wall thickness 0.71mm, as drawn, 99.9%
Copper, mesh, 300x300mm, nominal aperture 0.14mm, thickness 0.25mm, wire diameter 0.115mm, 100x100 wires/inch, open area 30.3%, plain weave mesh
Copper - O.F.H.C., rod, 100mm, diameter 3.15mm, as drawn, 99.95+%
Copper - O.F.H.C., tube, 200mm, outside diameter 2.54mm, inside diameter 1.54mm, wall thickness 0.5mm, 99.95+%
Copper - O.F.H.C., foil, 8mm disks, thickness 0.25mm, annealed, 99.95+%
Copper - O.F.H.C., foil, light tested, 150x150mm, thickness 0.010mm, hard, 99.95+%
Copper - O.F.H.C., sheet, 150x150mm, thickness 12.7mm, 99.99+%