901082
Carbon nanotube sheet
aligned, size × thickness 100 mm × 100 mm × 1-5 μm
Synonym(s):
MWCNT, MWNT, Multiwall carbon nanotube
Select a Size
| Size/SKU | Availability | Price |
|---|---|---|
1 ea | Check Cart for Availability | $1,090.00 |
About This Item
Quality Segment
assay
>95% (carbon)
resistivity
10-1000 Ω/sq
size × thickness
100 mm × 100 mm × 1-5 μm
diameter
10-40 nm (carbon nanotubes)
SMILES string
[C]
InChI
1S/C
InChI key
OKTJSMMVPCPJKN-UHFFFAOYSA-N
General description
CNT has a multi-walled structure. Crystal quality of CNT is examined by Raman scattering measurement. Intensity ratio of G-peak (1580 cm-1) and D-peak (1350 cm-1) represents quality of graphitization of carbon materials. G/D of CNT is ∼3, showing high crystal quality. The high crystallinity is supported by transmission electron microscopy.
Preparation Note
1 of 1
This Item | |||
|---|---|---|---|
| description aligned, size × thickness 100 mm × 100 mm × 1-5 μm | description ≥90% carbon basis (≥70% as carbon nanotubes), 0.7-1.3 nm diameter | description aligned, size × thickness 50 mm × 50 mm × 1-5 μm | description 98% (Semiconducting), avg. no. of layers, 1 |
| assay >95% (carbon) | assay ≥90% carbon basis (≥70% as carbon nanotubes) | assay >95% (carbon) | assay 98% (Semiconducting), 2% (Metallic) |
| Quality Level 100 | Quality Level 200 | Quality Level 100 | Quality Level 100 |
| diameter 10-40 nm (carbon nanotubes) | diameter 0.7-1.3 nm | diameter 10-40 nm (carbon nanotubes) | diameter 1.2-1.7 nm |
| size × thickness 100 mm × 100 mm × 1-5 μm | size × thickness - | size × thickness 50 mm × 50 mm × 1-5 μm | size × thickness - |
| resistivity 10-1000 Ω/sq | resistivity - | resistivity 10-1000 Ω/sq | resistivity - |
Still not finding the right product?
Explore all of our products under Carbon nanotube sheet
Storage Class
11 - Combustible Solids
WGK
WGK 3
Flash Point (°F)
Not applicable
Flash Point (°C)
Not applicable
Choose from one of the most recent versions:
Already Own This Product?
Find documentation for the products that you have recently purchased in the Document Library.