808237
Aluminum-doped zinc oxide nanoparticle ink
2.5 wt. %, viscosity 2.2 cP, work function -3.9 eV
Sinonimo/i:
AZO ink, Al-doped ZnO dispersion, Al-dopend ZnO suspension, Al:ZnO ink, Avantama N-21X, Nanograde N-21X
Scegli un formato
| A voi/SKU | Disponibilità | Prezzo |
|---|---|---|
10 mL | Per informazioni sulla disponibilità, contatta il Servizio Clienti. | 135,00 € |
50 mL | Per informazioni sulla disponibilità, contatta il Servizio Clienti. | 455,00 € |
Informazioni su questo articolo
135,00 €
Quality Segment
form
dispersion
concentration
2.5 wt. % (crystalline Al doped ZnO (3.15 mol% Al) in mixture of alcohols)
work function
-3.7--4.1 eV
particle size
8-16 nm
viscosity
1.7-2.7 cP
Application
Preparation Note
- Storage: In dark at room temperature.
- Prior to application: Shake, ultrasonicate with sonic horn and (optionally) filter through 0.45μm PTFE filter.
- Post-treatment: Annealing of deposited Al doped ZnO films at 80°C - 120°C.
Legal Information
1 of 1
Questo articolo | ||
|---|---|---|
| particle size 8-16 nm | particle size 8-16 nm | particle size 8-16 nm |
| form dispersion | form dispersion | form dispersion |
| viscosity 1.7-2.7 cP | viscosity 1.6-2.6 cP | viscosity 8-14 cP |
| Quality Level 100 | Quality Level 100 | Quality Level 100 |
| concentration 2.5 wt. % (crystalline Al doped ZnO (3.15 mol% Al) in mixture of alcohols) | concentration 2.5 wt. % (crystalline ZnO in isopropanol) | concentration 2.5 wt. % (crystalline ZnO in isopropanol and propylene glycol) |
| work function -3.7--4.1 eV | work function -3.7--4.1 eV | work function -4.1--4.5 eV |
Still not finding the right product?
Explore all of our products under Aluminum-doped zinc oxide nanoparticle ink
signalword
Danger
hcodes
Hazard Classifications
Aquatic Chronic 2 - Eye Irrit. 2 - Flam. Liq. 2 - STOT SE 3
target_organs
Central nervous system
Classe di stoccaggio
3 - Flammable liquids
wgk
WGK 2
flash_point_f
60.8 °F
flash_point_c
16 °C
Scegli una delle versioni più recenti:
Possiedi già questo prodotto?
I documenti relativi ai prodotti acquistati recentemente sono disponibili nell’Archivio dei documenti.