蒸汽壓力
1 mmHg ( 487 °C)
化驗
99.99%
形狀
foil
製造商／商標名
Goodfellow 190-680-37
電阻係數
5.8 μΩ-cm, 20°C
直徑× 厚度
8 mm × 0.25 mm
bp
907 °C (lit.)
mp
420 °C (lit.)
密度
7.133 g/mL at 25 °C (lit.)
SMILES 字串
[Zn]
InChI
1S/Zn
InChI 密鑰
HCHKCACWOHOZIP-UHFFFAOYSA-N
1 of 4
本產品 | GF25289837 | GF44141712 | GF80845881 |
|---|---|---|---|
| assay 99.99% | assay 99.99% | assay 99.99% | assay 99.99% |
| manufacturer/tradename Goodfellow 190-680-37 | manufacturer/tradename Goodfellow 252-898-37 | manufacturer/tradename Goodfellow 441-417-12 | manufacturer/tradename Goodfellow 808-458-81 |
| form foil | form foil | form foil | form foil |
| mp 420 °C (lit.) | mp 420 °C (lit.) | mp 420 °C (lit.) | mp 420 °C (lit.) |
| resistivity 5.8 μΩ-cm, 20°C | resistivity 5.8 μΩ-cm, 20°C | resistivity 5.8 μΩ-cm, 20°C | resistivity 5.8 μΩ-cm, 20°C |
| density 7.133 g/mL at 25 °C (lit.) | density 7.133 g/mL at 25 °C (lit.) | density 7.133 g/mL at 25 °C (lit.) | density 7.133 g/mL at 25 °C (lit.) |
一般說明
For updated SDS information please visit www.goodfellow.com.
法律資訊
Product of Goodfellow
Zhengquan Li et al.
Chemistry (Weinheim an der Bergstrasse, Germany), 10(22), 5823-5828 (2004-10-09)
A solution surface-erosion route was successfully employed to produce one-dimensional (1D) ZnO nanostructures. ZnO nanorod arrays and three-dimensional urchin-like assemblies could be selectively obtained with different manipulations. In this process, zinc foil was introduced to an organic solution system and
Yang Liu et al.
Chemistry (Weinheim an der Bergstrasse, Germany), 13(23), 6667-6673 (2007-05-31)
Well-aligned zinc oxide microrod and microtube arrays with high aspect ratios were fabricated on zinc foil by a simple solution-phase approach in an aqueous solution of ethylenediamine (en). The shape of the ZnO microstructures can be easily modulated from rods
Huibo Chen et al.
Nanoscale research letters, 5(3), 570-575 (2009-01-01)
We reported the optical and wettability properties of aligned zinc oxide micro/nanotube arrays, which were synthesized on zinc foil via a simple hydrothermal method. As-synthesized ZnO micro/nanotubes have uniform growth directions along the [0001] orientations with diameters in the range
Pritesh Hiralal et al.
ACS nano, 4(5), 2730-2734 (2010-04-27)
Solid-state and flexible zinc carbon (or Leclanche) batteries are fabricated using a combination of functional nanostructured materials for optimum performance. Flexible carbon nanofiber mats obtained by electrospinning are used as a current collector and cathode support for the batteries. The
Hongqin Liu et al.
ACS applied materials & interfaces, 1(9), 2086-2091 (2010-04-02)
Zinc, silicon, and steel superhydrophobic surfaces were prepared by a simple solution-immersion technique. In the case of zinc, the method consists of dipping of the substrate in a prehydrolyzed methanol solution of 1H,1H,2H,2H-(perfluorooctyl)trichlorosilane [CF(3)(CF(2))(5)(CH(2))(2)SiCl(3), PFTS] for 24 h at 50
Active Filters
我們的科學家團隊在所有研究領域都有豐富的經驗，包括生命科學、材料科學、化學合成、色譜、分析等.
聯絡技術服務