Preparation of single phase Zn2TiO4 spinel from a new ZnTi layered double hydroxide precursor.

Preparation of single phase Zn2TiO4 spinel from a new ZnTi layered double hydroxide precursor.

Journal of nanoscience and nanotechnology (2014-04-18)

Jianye Song, Mingzhe Leng, Hongdi Xiao, Liangji Zhang, Yaowei Qin, Wanguo Hou, Na Du, Jianqiang Liu

ABSTRACT

A single-source ZnTi-layered double hydroxide precursor was used to prepare single phase Zn2TiO4. This approach involves two steps: the calcination of a ZnTi-layered double hydroxide precursor and selective leaching zinc oxide from the resultant calcined products. The materials were characterized by X-ray diffraction (XRD), scanning electron microscope (SEM) thermogravimetric and differential thermal analysis (TG-DTA), transmission electron microscope (TEM), surface area measurement and UVvis diffuse reflection spectroscopy. The results indicated that a single phase Zn2TiO4 could be successfully obtained from a ZnTi-layered double hydroxide precursor at a relatively low temperature in short calcination time. The TEM and SEM show that the diameter of Zn2TiO4 particles prepared at 900 degrees C is in the range of 20-100 nm and smaller than that prepared by the solid-state method. UV-Vis diffuse reflection spectroscopy demonstrates that the material has an energy bandgap around 3.7 eV.

MATERIALS

Product Number

Brand

Product Description

499552

Sigma-Aldrich

Zinc preparation, 5 g/dL Zn²⁺ in THF, highly reactive Rieke^®metal

369489

Sigma-Aldrich

Titanium, foil, thickness 2.0 mm, 99.7% trace metals basis

266035

Sigma-Aldrich

Titanium, wire, diam. 1.0 mm, 99.99% trace metals basis

578002

Sigma-Aldrich

Zinc, nanopowder, 40-60 nm avg. part. size, ≥99% trace metals basis

348791

Sigma-Aldrich

Titanium, foil, thickness 0.127 mm, 99.7% trace metals basis

348848

Sigma-Aldrich

Titanium, foil, thickness 0.025 mm, 99.98% trace metals basis

248576

Sigma-Aldrich

Titanium(IV) oxide, anatase, powder, −325 mesh, ≥99% trace metals basis

204757

Sigma-Aldrich

Titanium(IV) oxide, rutile, ≥99.98% trace metals basis

232033

Sigma-Aldrich

Titanium(IV) oxide, anatase, powder, 99.8% trace metals basis

266361

Sigma-Aldrich

Zinc, sticks, diam. 7-10 mm, 99.97% trace metals basis

266353

Sigma-Aldrich

Zinc, pieces, 2-14 mesh, 99.9% trace metals basis

267619

Sigma-Aldrich

Zinc, foil, thickness 0.25 mm, 99.999% trace metals basis

349410

Sigma-Aldrich

Zinc, foil, thickness 1.0 mm, 99.99% trace metals basis

243469

Sigma-Aldrich

Zinc, granular, 20-30 mesh, ACS reagent, ≥99.8%

267635

Sigma-Aldrich

Zinc, shot, 5 mm, 99.999% trace metals basis

305812

Sigma-Aldrich

Titanium, ≤10 mm, ≥99.99% trace metals basis (purity exclusive of Na and K content)

460400

Sigma-Aldrich

Titanium, wire, diam. 0.25 mm, 99.7% trace metals basis

IRMM531C

Titanium, IRMM^®, certified reference material, 0.5 mm wire

IRMM531B

Titanium, IRMM^®, certified reference material, 0.5 mm foil

31653

Sigma-Aldrich

Zinc, puriss. p.a., ACS reagent, reag. ISO, reag. Ph. Eur., ≥99.9%, granular

209988

Sigma-Aldrich

Zinc, dust, <10 μm, ≥98%

267902

Sigma-Aldrich

Titanium, wire, diam. 0.81 mm, 99.7% trace metals basis

402583

Sigma-Aldrich

Zinc, shot, <12 mm, 99.99% trace metals basis

204730

Sigma-Aldrich

Titanium(IV) oxide, rutile, 99.995% trace metals basis

224227

Sigma-Aldrich

Titanium(IV) oxide, rutile, powder, <5 μm, ≥99.9% trace metals basis

637262

Sigma-Aldrich

Titanium(IV) oxide, rutile, nanopowder, <100 nm particle size, 99.5% trace metals basis

634662

Sigma-Aldrich

Titanium(IV) oxide, mixture of rutile and anatase, nanopowder, <100 nm particle size (BET), 99.5% trace metals basis

700347

Sigma-Aldrich

Titanium(IV) oxide, mixture of rutile and anatase, nanoparticles, <150 nm particle size (volume distribution, DLS), dispersion, 40 wt. % in H₂O, 99.5% trace metals basis

637254

Sigma-Aldrich

Titanium(IV) oxide, anatase, nanopowder, <25 nm particle size, 99.7% trace metals basis

GF51463357

Titanium, tube, 200mm, outside diameter 10.3mm, inside diameter 8.7mm, wall thickness 0.8mm, annealed, 99.6+%